Modes of flip chip solder joints under high electric current stressing

被引：0
|
作者：
Ye, H [1 ]
Basaran, C [1 ]
Hopkins, DC [1 ]
机构：
[1] SUNY Buffalo, UB Elect Packaging Lab, Buffalo, NY 14260 USA
来源：
2003 INTERNATIONAL SYMPOSIUM ON MICROELECTRONICS | 2003年 / 5288卷
关键词：
failure modes; flip chip; solder joint; electromigration; thermomigration; current stressing;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The failure modes of flip chip solder joints under current stressing are analyzed based on the experiments of 19 flip chip modules. Three different failure modes were reported. Among them, only Mode 3 failure is caused by the combined effect of electromigration and thermomigration, where void nucleation and growth contribute to the ultimate failure of the module. The void nucleation and growth in solder joint during current stressing is discussed in detail. The Ni UBM-solder interface is found to be the favorite site of voids nucleation and growth. The effect of pre-existing voids on the failure process of a solder joint is found to be dependent on their location.
引用
收藏
页码：801 / 806
页数：6
相关论文
共 50 条
  • [21] Thermomigration in Pb-Sn solder joints under joule heating during electric current stressing
    Ye, H
    Basaran, C
    Hopkins, D
    APPLIED PHYSICS LETTERS, 2003, 82 (07) : 1045 - 1047
  • [22] Thermal gradient in solder joints under electrical-current stressing
    Shao, TL
    Chiu, SH
    Chen, C
    Yao, DJ
    Hsu, CY
    JOURNAL OF ELECTRONIC MATERIALS, 2004, 33 (11) : 1350 - 1354
  • [23] Thermal gradient in solder joints under electrical-current stressing
    T. L. Shao
    S. H. Chiu
    Chih Chen
    D. J. Yao
    C. Y. Hsu
    Journal of Electronic Materials, 2004, 33 : 1350 - 1354
  • [24] Experimental Evidence for Formation of Ni-Al Compound in Flip-Chip Joints Under Current Stressing
    Tsai, M. Y.
    Lin, Y. L.
    Tsai, M. H.
    Chen, Y. J.
    Kao, C. R.
    JOURNAL OF ELECTRONIC MATERIALS, 2011, 40 (10) : 2076 - 2080
  • [25] Experimental Evidence for Formation of Ni-Al Compound in Flip-Chip Joints Under Current Stressing
    M. Y. Tsai
    Y. L. Lin
    M. H. Tsai
    Y. J. Chen
    C. R. Kao
    Journal of Electronic Materials, 2011, 40 : 2076 - 2080
  • [26] Effect of electric current stressing on mechanical performance of solders and solder joints: A review
    Bo Wang
    Wangyun Li
    Shuye Zhang
    Xingmin Li
    Kailin Pan
    Journal of Materials Science, 2022, 57 : 17533 - 17562
  • [27] Effect of electric current stressing on mechanical performance of solders and solder joints: A review
    Wang, Bo
    Li, Wangyun
    Zhang, Shuye
    Li, Xingmin
    Pan, Kailin
    JOURNAL OF MATERIALS SCIENCE, 2022, 57 (37) : 17533 - 17562
  • [28] Electromigration Reliability With Respect to Cu Weight Contents of Sn-Ag-Cu Flip-Chip Solder Joints Under Comparatively Low Current Stressing
    Lai, Yi-Shao
    Chiu, Ying-Ta
    JOURNAL OF ELECTRONIC PACKAGING, 2008, 130 (04)
  • [29] Failure mechanism of Sn-Ag-Cu flip-chip solder joints with different Cu weight contents under comparatively low current stressing
    Lai, Yi-Shao
    Chiu, Ying-Ta
    57TH ELECTRONIC COMPONENTS & TECHNOLOGY CONFERENCE, 2007 PROCEEDINGS, 2007, : 1462 - +
  • [30] The time-dependent melting failure in flip chip lead-free solder interconnects under current stressing
    Yang, D.
    Chan, Y. C.
    Tu, K. N.
    APPLIED PHYSICS LETTERS, 2008, 93 (04)
12345