STRUCTURAL DEFECTS OF INITIAL CRYSTALLIZATION AREAS IN SINGLE-CRYSTALLINE TURBINE BLADES

The as-cast single-crystalline turbine blades made of CMSX-4 superalloy were studied. The blades were obtained by the Bridgman technique at a withdrawal rate of 5mm/min. The as-cast samples were prepared by cutting the blade root with a fragment of selector. The dendritic structure of obtained samples was studied by Scanning Electron Microscopy. The crystal orientation and lattice parameters were analyzed by Omega-scan mapping method. Additionally, the X-ray diffraction topography was applied. It was found that the most structural defects are created in the areas where a change in the shape and dimensions of the blades occur. Even minor changes in their geometry and the unevenness of mold walls may also affect the formation of defects.