Composites reinforced by Al-Cu-Fe quasicrystalline particles with a copper matrix and their tribological properties

Copper-based composite coatings with addition of 34 wt % of Al-Cu-Fe quasicrystalline powder of dispersity less than 20 fum, as well as 70 wt % of quasicrystalline powder of dispersity less than 40fum and less than 3 fum, were produced by the cold spray process. The phase composition during annealing of samples at various temperatures was studied by X-ray phase analysis. Tribological properties of each composite coating and pure copper were investigated. The experimental results showed a considerable improvement of the tribological properties of the material at the addition of quasicrystals. The least wear was observed in the composite sample containing quasicrystalline inclusions of less than 3 fum subjected to thermal treatment. In this case the counterbody wear was practically absent.