Laboratory Experimental Study on Polymer Flooding in High-Temperature and High-Salinity Heavy Oil Reservoir

Polyacrylamide (HPAM) and other traditional polymers have poor temperature resistance and salinity tolerance and do not meet the needs of high-temperature and high-salinity reservoirs. In this study, a new temperature-resistant and salinity-tolerant polymer QJ75-39 was synthesized using acrylamide (AM) as a hydrophilic monomer, 1-acrylamide-2-methylpropanesulfonic acid (AMPS) and N-vinylpyrrolidone (NVP) as functional monomers and DS-16 as a hydrophobic monomer. Through laboratory experiments, the properties (temperature resistance, salinity tolerance and aging stability), polymer injection and core displacement effect of the polymer were studied. The experimental results showed that the new polymer could meet the needs of polymer flooding technology in high-temperature and high-salinity reservoirs. Experiments showed that the polymer had a temperature resistance of 95 degrees C and a salinity tolerance of 1.66 x 10(5) mg/L. When the temperature was 95 degrees C and the TDS was 55,376.8 mg/L, the viscosity of the polymer was 31.3 mPa s, and the viscosity remained above 30 mPa center dot s after aging for 60 days. The polymer had good injectivity between 300 and 600 mD, and the injection pressure could reach equilibrium quickly. The oil recovery effectively increased with the grsowth in the amount of injected polymer. When the injection amount was 0.5 PV, the enhanced oil recovery was 20.65%. This study is of great significance for the application and popularization of polymer flooding technology in high-temperature and high-salinity reservoirs.