Fatigue crack growth in a Ti-48Al-2Mn-2Nb alloy produced by centrifugal spray deposition

被引：0
|
作者：
Chen, WZ [1 ]
Qian, KW [1 ]
Gu, HC [1 ]
Wang, ZG [1 ]
机构：
[1] Fuzhou Univ, Coll Mat, Fuzhou 350002, Peoples R China
来源：
FATIGUE '99: PROCEEDINGS OF THE SEVENTH INTERNATIONAL FATIGUE CONGRESS, VOLS 1-4 | 1999年
关键词：
D O I：
暂无
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Fatigue crack growth behaviors of Ti-48Al-2Mn-2Nb alloy produced by CSD and treated by HIP were investigated. Fatigue crack growth tests were conducted under load control at room temperature. The result shows that the fatigue crack growth resistance of CSD samples is better than that of HIP samples. It indicates that the lamellar structure for CSD has a better resistance to crack growth than a duplex structure for HIP. Moreover, SEM observations of crack growth paths are shown that there are quite different models from CSD and HIP. The CSD samples show the main crack grows tortuously and discontinuously by ligaments bridging many microcracks in front of crack tip, while the smooth or almost straight crack path is found in HIP samples.
引用
收藏
页码：1579 / 1584
页数：6
相关论文
共 50 条
  • [31] HIGH-TEMPERATURE PHASE-TRANSFORMATION KINETICS AND THEIR EFFECTS ON DIFFUSION BONDING OF TI-48AL-2MN-2NB
    GODFREY, SP
    THREADGILL, PL
    STRANGWOOD, M
    JOURNAL DE PHYSIQUE IV, 1993, 3 (C7): : 485 - 488
  • [32] THE EFFECT OF HEAT-TREATMENT VARIABLES ON THE PHASE-TRANSFORMATIONS AT 1420-DEGREES-C IN TI-48AL AND TI-48AL-2MN-2NB ALLOYS
    RAMANUJAN, RV
    ACTA METALLURGICA ET MATERIALIA, 1995, 43 (12): : 4439 - 4451
  • [33] Fatigue crack growth mechanisms of cast Ti-48Al (at. %) alloy
    Hamada, S
    Nozue, A
    Tamin, MN
    DAMAGE AND FRACTURE MECHANICS VI: COMPUTER AIDED ASSESSMENT AND CONTROL, 2000, 6 : 203 - 212
  • [34] 离心喷射沉积Ti-48Al-2Mn-2Nb的疲劳裂纹扩展速率和门槛值
    陈文哲
    张飒
    钱匡武
    顾海澄
    王中光
    不详
    金属学报 , 1998, (01) : 70 - 74
  • [35] An investigation of the effects of temperature on fatigue crack growth in a cast lamellar Ti-45Al-2Mn-2Nb+0.8 vol.% TiB2 alloy
    Lou, J
    Mercer, C
    Soboyejo, WO
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 319 : 618 - 624
  • [36] Microstructural characterisation of fatigue crack growth fracture surfaces of lamellar Ti45Al2Mn2Nb1B
    Yang, J.
    Li, H.
    Hu, D.
    Dixon, M.
    INTERMETALLICS, 2014, 45 : 89 - 95
  • [37] Effects of test orientation on fracture and fatigue crack growth behavior of third generation as-cast Ti-48Al-2Nb-2Cr
    Dahar, Matthew S.
    Seifi, S. Mohsen
    Bewlay, B. P.
    Lewandowski, John J.
    INTERMETALLICS, 2015, 57 : 73 - 82
  • [38] STUDY OF MICROSTRUCTURES OF DEFORMED Ti-48Al-Mn-Nb ALLOY
    D Song
    Acta Metallurgica Sinica(English Letters), 1996, (04) : 267 - 271
  • [39] THE NATURE OF THE GAMMA-ALLOTRIOMORPH ALPHA(2) PLUS GAMMA-LAMELLAE INTERFACE FOR ELEVATED-TEMPERATURE TRANSFORMATIONS IN TI-48AL-2MN-2NB
    GODFREY, SP
    STRANGWOOD, M
    ELECTRON MICROSCOPY AND ANALYSIS 1993, 1993, (138): : 449 - 452
  • [40] Investigation of the influence of process parameters on crack formation and mechanisms in Ti-48Al-2Cr-2Nb alloy via laser directed energy deposition
    Cui, Baolei
    Liu, Weijun
    Bian, Hongyou
    Chen, KeQiang
    Xu, Xiaowen
    MATERIALS RESEARCH EXPRESS, 2023, 10 (12)
12345