Sintering effect on electrical properties of ZnO-V2O5-MnO2-Nb2O5 ceramics

被引：17
|
作者：
Nahm, Choon-W. [1 ]
机构：
[1] Dong Eui Univ, Dept Elect Engn, Semicond Ceram Lab, Pusan 614714, South Korea
来源：
JOURNAL OF ALLOYS AND COMPOUNDS | 2011年 / 509卷 / 34期
关键词：
Ceramics; Sintering; Electrical properties; Varistors; NONOHMIC PROPERTIES; MICROSTRUCTURE; VARISTORS;
D O I：
10.1016/j.jallcom.2011.06.065
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
The microstructure and electrical properties of quaternary ZnO-V2O5-MnO2-Nb2O5 ceramics were investigated at different sintering temperature (875-950 degrees C). The average grain size increased from 4.4 mu m to 9.6 mu m with increasing sintering temperature. The breakdown field decreased from 6991 V/cm to 943 V/cm with increasing sintering temperature. Proper sintering for quaternary ZnO-V2O5-MnO2-Nb2O5 ceramics led to surprisingly high nonlinear coefficient (50). The donor concentration increased from 3.33 x 10(17) cm(-3) to 7.64 x 10(17) cm(-3) with increasing sintering temperature and the barrier height exhibited the maximum value (1.07 eV) at 900 degrees C. (C) 2011 Elsevier B.V. All rights reserved.
引用
下载
收藏
页码：L314 / L317
页数：4
相关论文
共 50 条
12345