Fracture of the Surface Layers of Alumina Ceramics under the Action of a High-Power Ion Beam of Nanosecond Duration

被引：1
|
作者：
Kovivchak, V. S. [1 ]
Panova, T. V. [1 ]
机构：
[1] Dostoevsky Omsk State Univ, Omsk 644077, Russia
来源：
JOURNAL OF SURFACE INVESTIGATION | 2019年 / 13卷 / 06期
关键词：
high-power ion beam; alumina ceramic; surface morphology; fracture; composition; SINGLE-CRYSTAL SILICON; ALLOY;
D O I：
10.1134/S1027451019060363
中图分类号：
O469 [凝聚态物理学];
学科分类号：
070205 ;
摘要：
The fracture of surface layers of alumina ceramic (polycor) under the action of a high-power ion beam of nanosecond duration is investigated. The characteristic features of such fracture are determined. An estimation of the thickness of breakaway fragments of the surface layer of the ceramics gives values in the range from 4 to 12 mu m at single high-power ion beam irradiation with a current density of 150 A/cm(2). Oxygen depletion in the surface layer of the ceramics is established. The effect of irradiation on the structural-phase state of the ceramics is considered. The possible mechanisms of the observed fracture are discussed.
引用
收藏
页码：1252 / 1255
页数：4
相关论文
共 50 条
  • [31] Modifying the composition of a brass and bronze surface layer under a high power ion beam of a nanosecond duration
    V. S. Kovivchak
    T. V. Panova
    K. A. Mikhailov
    E. V. Knyazev
    Technical Physics Letters, 2013, 39 : 59 - 62
  • [32] Surface modification of bismuth and tin under the action of a powerful ion beam of nanosecond duration
    V. S. Kovivchak
    T. V. Panova
    K. A. Mikhailov
    Journal of Surface Investigation. X-ray, Synchrotron and Neutron Techniques, 2012, 6 : 248 - 250
  • [33] Surface modification of bismuth and tin under the action of a powerful ion beam of nanosecond duration
    Kovivchak, V. S.
    Panova, T. V.
    Mikhailov, K. A.
    JOURNAL OF SURFACE INVESTIGATION-X-RAY SYNCHROTRON AND NEUTRON TECHNIQUES, 2012, 6 (02) : 248 - 250
  • [34] Ultrafast catalytic synthesis of carbon nanofibers on a surface of commercial chlorinated polymers under the action of a high power ion beam of nanosecond duration
    Kovivchak, Vladimir S.
    Kryazhev, Yurii G.
    Trenikhin, Mikhail, V
    Arbuzov, Aleksey B.
    Zapevalova, Evgenia S.
    Likholobov, Vladimir A.
    APPLIED SURFACE SCIENCE, 2018, 448 : 642 - 645
  • [35] Modification of carbon films by high-power proton-carbon ion beam of nanosecond duration
    V. S. Kovivchak
    T. V. Panova
    O. V. Krivozubov
    N. A. Davletkil’deev
    Journal of Surface Investigation. X-ray, Synchrotron and Neutron Techniques, 2011, 5 : 246 - 248
  • [36] Modification of carbon films by high-power proton-carbon ion beam of nanosecond duration
    Kovivchak, V. S.
    Panova, T. V.
    Krivozubov, O. V.
    Davletkil'deev, N. A.
    JOURNAL OF SURFACE INVESTIGATION, 2011, 5 (02): : 246 - 248
  • [37] Periodical structure formation on a magnesium and aluminum surface under high power ion beam irradiation of nanosecond duration
    V. S. Kovivchak
    T. V. Panova
    K. A. Mikhailov
    Journal of Surface Investigation. X-ray, Synchrotron and Neutron Techniques, 2012, 6 : 64 - 66
  • [38] Periodical structure formation on a magnesium and aluminum surface under high power ion beam irradiation of nanosecond duration
    Kovivchak, V. S.
    Panova, T. V.
    Mikhailov, K. A.
    JOURNAL OF SURFACE INVESTIGATION-X-RAY SYNCHROTRON AND NEUTRON TECHNIQUES, 2012, 6 (01) : 64 - 66
  • [39] Formation of Carbon Nanofibers on the Surface of a Photoresist under the Action of a Powerful Ion Beam of Nanosecond Duration
    Kovivchak, V. S.
    JOURNAL OF SURFACE INVESTIGATION, 2021, 15 (05): : 1087 - 1091
  • [40] Formation of Carbon Nanofibers on the Surface of a Photoresist under the Action of a Powerful Ion Beam of Nanosecond Duration
    V. S. Kovivchak
    Journal of Surface Investigation: X-ray, Synchrotron and Neutron Techniques, 2021, 15 : 1087 - 1091
12345