Stress-modulated optimization of polymorphic phase transition in Li-doped (K,Na)NbO3

The effect of uniaxial compressive stress on the crystal structure of a 6mol. % Li-doped (K,Na)NbO3 (LKNN6a) ceramic was investigated using in situ synchrotron X-ray diffraction, revealing the stress-induced relative change in monoclinic Pm and tetragonal P4mm phases. As such, stress-induced phase transformations, in addition to the lattice deformation and domain switching, are the contributing factors for the observed macroscopic mechanical behavior of LKNN6a. The in situ stress-dependent diffraction data also demonstrates a method to mechanically modulate the polymorphic phase transition temperature (T-PPT) to a higher temperature, as observed by the temperature-dependent permittivity measurements under a constant bias stress. The external uniaxial compressive stress increases the stability of the lower symmetry monoclinic phase, shifting T-PPT to a higher temperature by 60 degrees C for the maximum uniaxial compressive stress of 300MPa in the studied composition. Importantly, the stress-induced stabilization of the room-temperature ferroelectric phase can be useful to optimize the phase transition region, as well as increase the temperature stability of lead-free KNN.