Experimental Analysis and Damage Modeling of High-Density Polyethylene under Fatigue Loading

被引：15

作者：

Djebli, A. ^{[1
]}

Bendouba, M. ^{[1
]}

Aid, A. ^{[1
]}

Talha, A. ^{[2
,3
]}

Benseddiq, N. ^{[2
]}

Benguediab, M. ^{[4
]}

机构：

[1] Univ Mustapha Stambouli, Fac Sci & Technol, LPQ3M, Mascara, Algeria

[2] Univ Lille 1, LML, Dept Genie Mecan, F-59655 Villeneuve Dascq, France

[3] Ecole Hautes Etud Ingn, HEI, Paris, France

[4] Univ Sidi Bel Abess, Fac Technol, Sidi Bel Abbes, Algeria

来源：

ACTA MECHANICA SOLIDA SINICA | 2016年 / 29卷 / 02期

关键词：

HDPE; semi-crystalline; damage accumulation; stiffness degradation; CRACK-PROPAGATION; ALUMINUM-ALLOY; BEHAVIOR; FRACTURE; ACCUMULATION; PREDICTION; MECHANICS; FAILURE; POLYMER; TENSILE;

D O I：

10.1016/S0894-9166(16)30102-1

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this study, an experimental analysis for determining the fatigue strength of HDPE-100 under cyclic loading is presented. The curve of cumulative fatigue damage versus number of cycles (D-N) was deduced from stiffness degradation. Based on the three stage damage trend, the remaining fatigue life is numerically predicted by considering a double term power damage accumulation model. This model is found to be accurate, both in modeling the rapid damage growth in the early life and near the end of the fatigue life. Numerical results illustrate that the proposed model is capable of accurately fitting several different sets of experimental data.

引用

页码：133 / 144

页数：12

共 50 条

[21] ENVIRONMENTAL DYNAMIC FATIGUE CRACK-PROPAGATION IN HIGH-DENSITY POLYETHYLENE - AN EMPIRICAL MODELING APPROACH
ELHAKEEM, HM
CULVER, LE
INTERNATIONAL JOURNAL OF FATIGUE, 1981, 3 (01) : 3 - 8
[22] Multiaxial Fatigue Behavior of High-Density Polyethylene (HDPE) Including Notch Effect: Experiments and Modeling
Amjadi, Mohammadreza
Fatemi, Ali
ICMFF12 - 12TH INTERNATIONAL CONFERENCE ON MULTIAXIAL FATIGUE AND FRACTURE, 2019, 300
[23] FATIGUE CRACK-PROPAGATION IN HIGH-DENSITY POLYETHYLENE AND POLYPROPYLENE
SHEU, C
GOOLSBY, RD
ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1983, 185 (MAR): : 176 - ORPL
[24] Cyclic viscoplasticity of high-density polyethylene: Experiments and modeling
Drozdov, A. D.
deC. Christiansen, J.
COMPUTATIONAL MATERIALS SCIENCE, 2007, 39 (02) : 465 - 480
[25] ANALYSIS OF FATIGUE BEHAVIOR OF HIGH-DENSITY POLYETHYLENE BASED ON DYNAMIC VISCOELASTIC MEASUREMENTS DURING THE FATIGUE PROCESS
TAKAHARA, A
YAMADA, K
KAJIYAMA, T
TAKAYANAGI, M
JOURNAL OF APPLIED POLYMER SCIENCE, 1981, 26 (04) : 1085 - 1104
[26] Creep behavior and modeling of high-density polyethylene (HDPE)
Amjadi, Mohammad
Fatemi, Ali
POLYMER TESTING, 2021, 94
[27] Experimental analysis of thermal and damage evolutions of DCFC under static and fatigue loading
Bale, Jefri
Valot, Emmanuel
Monin, Martine
Polit, Olivier
Bathias, Claude
Soemardi, Tresna
REVUE DES COMPOSITES ET DES MATERIAUX AVANCES-JOURNAL OF COMPOSITE AND ADVANCED MATERIALS, 2016, 26 (02): : 165 - 184
[28] HIGH-DENSITY POLYETHYLENE
BESTGEN, F
KUNSTSTOFFE-GERMAN PLASTICS, 1989, 79 (10): : 904 - 905
[29] High-density polyethylene
不详
MODERN PLASTICS, 1996, 73 (11): : 116 - 116
[30] HIGH-DENSITY POLYETHYLENE
ALVINE, R
PLASTICS WORLD, 1971, 29 (08): : 50 - &

← 1 2 3 4 5 →