Characteristic of Low Temperature Carburized Austenitic Stainless Steel

被引：4
|
作者：
Istiroyah [1 ]
Pamungkas, M. A. [1 ]
Saroja, G. [1 ]
Ghufron, M. [1 ]
Juwono, A. M. [1 ]
机构：
[1] Brawijaya Univ, Fac Nat Sci, Phys Dept, Malang, Indonesia
来源：
INTERNATIONAL CONFERENCE ON CHEMISTRY AND MATERIAL SCIENCE (IC2MS) 2017 | 2018年 / 299卷
关键词：
D O I：
10.1088/1757-899X/299/1/012048
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
Low temperature carburizing process has been carried out on austenitic stainless steel (ASS) type AISI 316L, that contain chromium in above 12 at%. Therefore, conventional heat treatment processes that are usually carried out at high temperatures are not applicable. The sensitization process due to chromium migration from the grain boundary will lead to stress corrosion crack and decrease the corrosion resistance of the steel. In this study, the carburizing process was carried out at low temperatures below 500 degrees C. Surface morphology and mechanical properties of carburized specimens were investigated using optical microscopy, non destructive profilometer, and Vicker microhardness. The surface roughness analysis show the carburising process improves the roughness of ASS surface. This improvement is due to the adsorption of carbon atoms on the surface of the specimen. Likewise, the hardness test results indicate the carburising process increases the hardness of ASS.
引用
收藏
页数：5
相关论文
共 50 条
  • [1] Carbide precipitation in austenitic stainless steel carburized at low temperature
    Ernst, F.
    Cao, Y.
    Michal, G. M.
    Heuer, A. H.
    [J]. ACTA MATERIALIA, 2007, 55 (06) : 1895 - 1906
  • [2] Enhanced Carbon Diffusion in Austenitic Stainless Steel Carburized at Low Temperature
    Ernst, F.
    Avishai, A.
    Kahn, H.
    Gu, X.
    Michal, G. M.
    Heuer, A. H.
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2009, 40A (08): : 1768 - 1780
  • [3] Thermal stability of low-temperature-carburized austenitic stainless steel
    Wang, Jun
    Li, Zhen
    Wang, Danqi
    Qiu, Shaoyu
    Ernst, Frank
    [J]. ACTA MATERIALIA, 2017, 128 : 235 - 240
  • [4] Enhanced Carbon Diffusion in Austenitic Stainless Steel Carburized at Low Temperature
    F. Ernst
    A. Avishai
    H. Kahn
    X. Gu
    G.M. Michal
    A.H. Heuer
    [J]. Metallurgical and Materials Transactions A, 2009, 40 : 1768 - 1780
  • [5] Effect of molybdenum on hardness of low-temperature plasma carburized austenitic stainless steel
    Tsujikawa, M.
    Noguchi, S.
    Yamauchi, N.
    Ueda, N.
    Sone, T.
    [J]. SURFACE & COATINGS TECHNOLOGY, 2007, 201 (9-11): : 5102 - 5107
  • [6] Mechanical properties and cracking behavior of low-temperature gaseous carburized austenitic stainless steel
    Jiang, Yong
    Li, Yang
    Peng, Yawei
    Gong, Jianming
    [J]. SURFACE & COATINGS TECHNOLOGY, 2020, 403
  • [7] Structure and properties of low temperature plasma carburized austenitic stainless steels
    Souza, R. M.
    Ignat, M.
    Pinedo, C. E.
    Tschiptschin, A. P.
    [J]. SURFACE & COATINGS TECHNOLOGY, 2009, 204 (6-7): : 1102 - 1105
  • [8] Colossal carbon supersaturation in austenitic stainless steels carburized at low temperature
    Cao, Y
    Ernst, F
    Michal, GM
    [J]. ACTA MATERIALIA, 2003, 51 (14) : 4171 - 4181
  • [9] The carbide M7C3 in low-temperature-carburized austenitic stainless steel
    Ernst, Frank
    Li, Dingqiang
    Kahn, Harold
    Michal, Gary M.
    Heuer, Arthur H.
    [J]. ACTA MATERIALIA, 2011, 59 (06) : 2268 - 2276
  • [10] On surface carbides in low-temperature carburized austenitic stainless steels
    Maistro, Giulio
    Yao, Yiming
    Klement, Uta
    Nyborg, Lars
    Cao, Yu
    [J]. MATERIALS CHARACTERIZATION, 2020, 167
12345