Effect of retained austenite phase on springback of cold-rolled TRIP steel sheets

被引:15
|
作者
Kim, Sungil [2 ]
Lee, Youngseog [1 ]
机构
[1] Chung Ang Univ, Dept Mech Engn, Seoul 156756, South Korea
[2] POSCO Tech Res Lab, Sheet Prod & Proc Res Grp, Gwangyang, South Korea
关键词
Springback; TRIP steel; Retained austenite; Austempering; V-bending test;
D O I
10.1016/j.msea.2011.09.077
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
We examined the effects of retained austenite phase on the springback of cold-rolled transformation-induced plasticity (TRIP) steel sheets through a series of V-bending tests. Prior to testing, the intercritically annealed TRIP steel sheets were heat-treated at different austempering temperatures (300, 350 and 400 degrees C) to obtain three specimens with different retained austenite phase fractions. Results show that the amount of springback in TRIP steel decreased as the fraction of retained austenite phase increased. The amount of springback was reduced by about 30% when the fraction of retained austenite phase increased by 5%. When the area fractions of the retained austenite phase of TRIP steel were less than 3%, we observed micro-cracks in the near-surface points of a V-shaped specimen where compressive and tensile stresses were concentrated. The dependency of material's direction upon springback was very weak in the V-bending test where no constraint such as a blank holder exists during testing. (C) 2011 Elsevier B.V. All rights reserved.
引用
收藏
页码:218 / 224
页数:7
相关论文
共 50 条
  • [21] Effect of retained austenite on the microstructure and mechanical properties of cold-rolled medium-manganese Q&P steel
    Feng, Yan
    Jing, Cainian
    Lin, Tao
    Wu, Zhonglin
    Li, Zhaotong
    Zhao, Jingrui
    [J]. IRONMAKING & STEELMAKING, 2023, 50 (02) : 167 - 173
  • [22] MODELLING AND CHARACTERISATION OF BAINITE AND RETAINED AUSTENITE IN HOT ROLLED TRIP STEEL
    Suwanpinij, Piyada
    Li Xiaoxiao
    Prahl, Ulrich
    Bleck, Wolfgang
    [J]. METAL 2016: 25TH ANNIVERSARY INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS, 2016, : 628 - 634
  • [23] Effect of microstructure on elongation in cold-rolled high carbon steel sheets
    Fujita, T
    Kariya, N
    Nakamura, N
    Hosoya, Y
    [J]. TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2005, 91 (07): : 616 - 622
  • [24] Effect of morphology of retained austenite on strength and ductility of TRIP-aided steel sheets
    Hashimoto, S
    Kashima, T
    Ikeda, S
    Sugimoto, K
    [J]. TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2002, 88 (07): : 400 - 405
  • [25] PHOSPHATABILITY OF COLD-ROLLED STEEL SHEETS ADDED TITANIUM
    USUKI, N
    [J]. TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (13): : 1315 - 1315
  • [26] COLD-ROLLED STEEL SHEETS PRODUCED BY CONTINUOUS ANNEALING
    TAKECHI, H
    TAKAHASHI, N
    ABE, M
    KATOH, H
    [J]. JOURNAL OF METALS, 1984, 36 (07): : 25 - 25
  • [27] The production and practice of cold-rolled steel sheets for automobile
    ZHU Guosen
    [J]. Baosteel Technical Research, 2010, 4(S1) (S1) : 50 - 50
  • [28] ULTRASONIC MONITORING OF TEXTURE IN COLD-ROLLED STEEL SHEETS
    HIRAO, M
    HARA, N
    FUKUOKA, H
    FUJISAWA, K
    [J]. JOURNAL OF THE ACOUSTICAL SOCIETY OF AMERICA, 1988, 84 (02): : 667 - 672
  • [29] HIGH-STRENGTH COLD-ROLLED STEEL SHEETS
    STUWE, HP
    [J]. ZEITSCHRIFT FUR METALLKUNDE, 1981, 72 (11): : 746 - 751
  • [30] Effect of thermomechanical parameters on the microstructure and retained austenite characteristics in a hot-rolled TRIP steel
    Yin, Yunyang
    Fang, Fang
    Chen, Wei
    Fu, Yongtao
    [J]. MANUFACTURING SCIENCE AND TECHNOLOGY, PTS 1-3, 2011, 295-297 : 1294 - 1299