Aging Behavior of T91/10CrMo910 Dissimilar Steel Welded Joints

被引：0
|
作者：
Yao, Yuhong [1 ,2 ]
Wei, Jianfeng [1 ]
Liu, Jiangnan [2 ]
Wang, Zhengpin [2 ]
Jin, Yaohua [2 ]
机构：
[1] Xi An Jiao Tong Univ, State Key Lab Mech Behav Mat, Xian 710049, Peoples R China
[2] Xian Technol Univ, Sch Mat & Chem Engn, Xian 710032, Peoples R China
来源：
ADVANCES IN SUPERALLOYS, PTS 1 AND 2 | 2011年 / 146-147卷
关键词：
T91/10CrMo910 dissimilar steel welded joints; aging behavior; coarse lath martensite; carbide ripening; diffusion;
D O I：
10.4028/www.scientific.net/AMR.146-147.156
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The microstructure and property of T91/10CrMo910 dissimilar steel welded joints after one and two years service have been studied by OM, TEM, EDS and Vickers hardness test in this paper. The results showed that after one year service the microhardness of T91/10CrMo910 dissimilar steel welded joints increased clearly and after two years service chromium element diffused or transferred from the welding line or T91 matrix to 10CrMo910 matrix. Coarse lath martensite was the characteristic of the microstructure of T91/10CrMo910 dissimilar steel welded joints, and the martensite laths became fragment after one and two years service. More carbide particles had been observed after one year service than that after two year service, which had a good agreement with the results of the micro-Vickers hardness test.
引用
收藏
页码：156 / +
页数：2
相关论文
共 50 条
  • [21] 电站用P91与10CrMo910异种钢焊接工艺研究
    颜景梅
    邵靖利
    蒙乐勤
    管道技术与设备, 2005, (01) : 28 - 30
  • [22] Microstructure and mechanical behavior of P91 steel dissimilar welded joints made with IN718 filler
    Kumar, Sanjeev
    Pandey, Chandan
    Goyal, Amit
    INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2021, 190
  • [23] Microstructural Evolution on the T91 Dissimilar Metal Joints during Creep Rupture Tests
    Guangmin LUO
    JournalofMaterialsScience&Technology, 2004, (04) : 383 - 386
  • [24] EXAMINATIONS OF THE WELDED JOINT T91 STEEL AFTER SERVICE AT ELEVATED TEMPERATURE
    Golanski, G.
    Merda, A.
    Klimaszewska, K.
    Wieczorek, P.
    ARCHIVES OF METALLURGY AND MATERIALS, 2020, 65 (01) : 237 - 242
  • [25] Microstructures and mechanical properties of dissimilar T91/347H steel weldments
    Mittal, Rutash
    Sidhu, Buta Singh
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2015, 220 : 76 - 86
  • [26] Microstructure and Mechanical Property of T91/15-15Ti Dissimilar Steels Welded Joint
    Li J.
    Su X.
    Feng W.
    Ren Y.
    Du A.
    Yuanzineng Kexue Jishu/Atomic Energy Science and Technology, 2021, 55 (10): : 1844 - 1849
  • [27] Experimental Investigations on Magnetically Impelled Arc Butt Welded T91 Steel Tubes
    S. Vignesh
    P. Dinesh Babu
    V. Prasanna Venkatesh
    S. Martin Vinoth
    P. Marimuthu
    Transactions of the Indian Institute of Metals, 2017, 70 : 741 - 748
  • [28] Experimental Investigations on Magnetically Impelled Arc Butt Welded T91 Steel Tubes
    Vignesh, S.
    Babu, P. Dinesh
    Venkatesh, V. Prasanna
    Vinoth, S. Martin
    Marimuthu, P.
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2017, 70 (03) : 741 - 748
  • [29] On Repair of Welded Joints of Heat-Resistant T91/P91 Chromium Steels During Use
    Demenin M.F.
    Power Technology and Engineering, 2019, 53 (01): : 74 - 77
  • [30] INFLUENCE OF CREEP ON THE PRECIPITATE STRUCTURE UNDER CONDITIONS OF LONG-TERM CREEP .4. INVESTIGATION OF THE STEEL 10CRMO910
    SCHULZE, O
    SAUTHOFF, G
    ARCHIV FUR DAS EISENHUTTENWESEN, 1984, 55 (02): : 73 - 80
12345