Aging Behavior of T91/10CrMo910 Dissimilar Steel Welded Joints

被引:0
|
作者
Yao, Yuhong [1 ,2 ]
Wei, Jianfeng [1 ]
Liu, Jiangnan [2 ]
Wang, Zhengpin [2 ]
Jin, Yaohua [2 ]
机构
[1] Xi An Jiao Tong Univ, State Key Lab Mech Behav Mat, Xian 710049, Peoples R China
[2] Xian Technol Univ, Sch Mat & Chem Engn, Xian 710032, Peoples R China
来源
ADVANCES IN SUPERALLOYS, PTS 1 AND 2 | 2011年 / 146-147卷
关键词
T91/10CrMo910 dissimilar steel welded joints; aging behavior; coarse lath martensite; carbide ripening; diffusion;
D O I
10.4028/www.scientific.net/AMR.146-147.156
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The microstructure and property of T91/10CrMo910 dissimilar steel welded joints after one and two years service have been studied by OM, TEM, EDS and Vickers hardness test in this paper. The results showed that after one year service the microhardness of T91/10CrMo910 dissimilar steel welded joints increased clearly and after two years service chromium element diffused or transferred from the welding line or T91 matrix to 10CrMo910 matrix. Coarse lath martensite was the characteristic of the microstructure of T91/10CrMo910 dissimilar steel welded joints, and the martensite laths became fragment after one and two years service. More carbide particles had been observed after one year service than that after two year service, which had a good agreement with the results of the micro-Vickers hardness test.
引用
收藏
页码:156 / +
页数:2
相关论文
共 50 条
  • [1] Analysis of the P91/10CrMo910 dissimilar steel welded joints
    Niu, Rui-Feng
    Meng, Wei-Ru
    Zhao, Jian-Cang
    Wang, Can-Gang
    Hanjie Xuebao, 8 (56-60):
  • [2] T91/10CrMo910焊接接头韧性分析
    于在松
    刘江南
    赵彦芬
    王正品
    张路
    石崇哲
    铸造技术, 2006, (11) : 1251 - 1254
  • [3] T91与10CrMo910异种钢焊接工艺分析
    李强
    中原工学院学报, 2006, (05) : 44 - 47
  • [4] Microstructures and Properties of Laser Hybrid Welded T91 Steel Joints after High Temperature Aging
    Hu Lianhai
    Liu Xiaolin
    Hou Debin
    Xu Changling
    Zhao Yang
    Fu Kun
    Wang Changcai
    CHINESE JOURNAL OF LASERS-ZHONGGUO JIGUANG, 2018, 45 (09):
  • [5] Microstructural and mechanical behavior in dissimilar T91/T22 welded pipes
    Mittal, Rutash
    Gupta, Ashutosh
    Pratap, Karan
    Shukla, Pratyush
    Gupta, Shyam
    Shanurrahman
    MATERIALS TODAY-PROCEEDINGS, 2020, 26 : 316 - 319
  • [6] In-situ detection of weld metal thermal cycle of 10CrMo910 steel
    Hu, Yanhua
    Chen, Furong
    Xie, Ruijun
    Li, Haitao
    Hanjie Xuebao/Transactions of the China Welding Institution, 2009, 30 (10): : 105 - 107
  • [7] Effect of creep degradation on the magnetic domain and magnetic properties of 10CrMo910 steel
    Zhang, Su-Zhou
    Tu, Shan-Tung
    FROM FAILURE TO BETTER DESIGN, MANFACTURE AND CONSTRUCTION, 2012, : 307 - 310
  • [8] P91与10CrMo910异种钢焊接技术试验
    牛锐锋
    赵健仓
    王淦刚
    孟卫如
    华东电力, 2003, (02) : 33 - 35
  • [9] Cracking of welded joints made of steel X10CrMoVNb9-1 (T91) - case study
    Lomozik, M.
    Zeman, M.
    Jachym, R.
    KOVOVE MATERIALY-METALLIC MATERIALS, 2012, 50 (04): : 285 - 294
  • [10] Microstructure and Failure Analysis of TP347H/T91 Dissimilar Steel Welded Piping
    Miao, Keji
    Liu, Jianfeng
    Yin, Yangyang
    Wang, Ting
    Sun, Ge
    Liu, Chuanhuai
    Shen, Li
    Ji, Dongmei
    Pan, Weiguo
    JOURNAL OF FAILURE ANALYSIS AND PREVENTION, 2022, 22 (02) : 578 - 586