Properties of Emulsion Paint with Modified Natural Rubber Latex/Polyvinyl Acetate Blend Binder

被引:3
|
作者
Ibrahim, Bahruddin [1 ]
Helwani, Zuchra [1 ]
Fadhillah, Ivan [1 ]
Wiranata, Arya [1 ]
Miharyono, Joni [2 ]
机构
[1] Univ Riau, Chem Engn Dept, Pekanbaru 28293, Indonesia
[2] Warna Indah Tirta Asia WITA, Pekanbaru 28291, Indonesia
来源
APPLIED SCIENCES-BASEL | 2022年 / 12卷 / 01期
关键词
emulsion paint binder; grafted natural rubber; liquid natural rubber; natural rubber latex; polyvinyl acetate; STYRENE; LATEX;
D O I
10.3390/app12010296
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
The direct use of natural rubber latex (NRL) as a binder for emulsion paints did not produce emulsion paints with good opacity, washability resistance, and regulated touch drying time, even when mixed with polyvinyl acetate (PVAc). This study aimed to study the properties of opacity (hiding power), washability resistance, and set drying touch time of emulsion paint with a binder added from a mixture of modified natural rubber latex (NRL) and PVAc. NRL modifications included UV photodepolymerization with TiO2 catalyst and grafting copolymerization of methyl methacrylate and styrene (NRL-g-(MMA-co-St)). NRL was mixed with PVAC at ratios of 0/100; 15/85; 25/75; 35/65; 50/50; 100/0% w/w before being used as a binder for emulsion paint. Emulsion paint samples had different binder contents, namely 2, 4, 6, and 8% w/w. Tests on paint samples included opacity using a UV-Vis spectrophotometer (EASYSPEC safas Monaco), washability using the Digital BGD 526 Wet Abrasion Scrub Tester, and drying time set using the ASTM STP500 procedure. The results showed that the opacity (hiding power), washability resistance, and set drying touch time met the emulsion paint standards for all binder levels, except the 100% w/w modified NRL composition. The higher level of NRL in the binder causes these properties to decrease and become unstable. The best opacity (hidden power), washing resistance, and drying touch time were obtained on modified NRL with a concentration of 15% w/w. The binder content in the paint was around 4% w/w, with an opacity of about 1.78% abs, washing resistance of 12 times, and the set drying touch time to 80 min.
引用
收藏
页数:9
相关论文
共 50 条
  • [31] Reinforcement of natural rubber latex with silica modified by cerium oxide: preparation and properties
    Zhang Fuquan
    Liao Lusheng
    Wang Yongzhou
    Wang Yueqiong
    Huang Honghai
    Li Puwang
    Peng Zheng
    Zeng Rizhong
    JOURNAL OF RARE EARTHS, 2016, 34 (02) : 221 - 226
  • [32] Mechanical and Thermal Properties of Natural Rubber Latex Modified by Purple Carbon Black
    Fan, Dan
    Liao, Xiaoxue
    Liao, Shuangquan
    Zhao, Yanfang
    Sun, Jie
    ADVANCES IN TEXTILE ENGINEERING AND MATERIALS III, PTS 1 AND 2, 2013, 821-822 : 961 - 964
  • [33] Experimental Investigation on the Properties of Vulcanized Natural Rubber-Modified Asphalt Binder
    Liu, Fei
    Pan, Baofeng
    Li, Zhuangzhuang
    Zhou, Changjun
    Xu, Shanwei
    JOURNAL OF TRANSPORTATION ENGINEERING PART B-PAVEMENTS, 2023, 149 (03)
  • [34] The use of natural rubber latex as a renewable and sustainable modifier of asphalt binder
    Wen, Yong
    Wang, Yuhong
    Zhao, Kecheng
    Sumalee, Agachai
    INTERNATIONAL JOURNAL OF PAVEMENT ENGINEERING, 2017, 18 (06) : 547 - 559
  • [35] Natural rubber latex as a new binder for slip casting of alumina ceramics
    Krishnan, P. P. Rakesh
    Kumar, P. Arun
    Prabhakaran, K.
    JOURNAL OF RUBBER RESEARCH, 2023, 26 (04) : 291 - 301
  • [36] Natural rubber latex as a new binder for slip casting of alumina ceramics
    P. P. Rakesh Krishnan
    P. Arun Kumar
    K. Prabhakaran
    Journal of Rubber Research, 2023, 26 : 291 - 301
  • [37] Aqueous tape casting of alumina using natural rubber latex binder
    Krishnan, Rakesh P. P.
    Vijayan, Sujith
    Wilson, Praveen
    Kumar, P. Arun
    Prabhakaran, K.
    CERAMICS INTERNATIONAL, 2019, 45 (15) : 18543 - 18550
  • [38] Properties of Natural Rubber/Chloroprene Rubber Blend for Rubber Fender Application: Effects of Blend Ratio
    Anggaravidya, Mahendra
    Amry, Akhmad
    Arti, Dewi K.
    Kalembang, Eryanti
    Susanto, Herri
    Hidayat, Ade S.
    Limansubroto, Caroline D.
    MACROMOLECULAR SYMPOSIA, 2020, 391 (01)
  • [39] Study on polypropylene/natural rubber blend with polystyrene-modified natural rubber as compatibilizer
    Hashim, AS
    Ong, SK
    POLYMER INTERNATIONAL, 2002, 51 (07) : 611 - 616
  • [40] Mechanical Properties of Natural rubber and Chloroprene Rubber Latex Blends
    Liao, XiaoXue
    Tan, HaiSheng
    Luo, MingChao
    Tang, Bing
    Liao, ShuangQuan
    Wei, XiaoDi
    ADVANCED MATERIALS, PTS 1-4, 2011, 239-242 : 1601 - +