Microstructure and fracture characteristics of spot-welded DP600 steel

被引：175
|
作者：
Ma, C. [1 ]
Chen, D. L. [1 ]
Bhole, S. D. [1 ]
Boudreau, G. [2 ]
Lee, A. [2 ]
Biro, E. [2 ]
机构：
[1] Ryerson Univ, Dept Mech & Ind Engn, Toronto, ON M5B 2K3, Canada
[2] Dofasco Ltd, Hamilton, ON L8N 3J5, Canada
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2008年 / 485卷 / 1-2期
基金：
加拿大创新基金会; 加拿大自然科学与工程研究理事会;
关键词：
resistance spot welding; expulsion; microstructure; mechanical properties; fatigue; fracture mode; dual-phase steel;
D O I：
10.1016/j.msea.2007.08.010
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Microstructural characterization, microhardness tests, tensile shear tests, and fatigue tests of spot-welded hot dipped galvanized (HDG) DP600 steel were conducted. The effects of weld expulsion on the microstructural characteristics, mechanical properties, and fracture modes were investigated using optical microscopy, image analysis and scanning electron microscopy (SEM) together with energy dispersive X-ray spectroscopy (EDS). The hardness in the weld nugget was observed to be over two times higher than that in the base metal due to the formation of lath martensite. Fatigue tests showed a slightly lower fatigue limit for the joints with the expulsion. The crack initiation was observed to occur basically at the boundary of the weld nugget and at the interface between two sheets. The causes for the interfacial fracture (IF) were discussed in relation to the microstructure and weld parameters. (C) 2007 Elsevier B.V. All rights reserved.
引用
收藏
页码：334 / 346
页数：13
相关论文
共 50 条
  • [21] EBSD Characterization of Microstructure and Micro-texture in a Friction Stir-Welded DP600 Steel
    Ashrafi, H.
    Shamanian, M.
    Sanayei, M.
    Farhadi, F.
    Szpunar, J. A.
    ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2023, 36 (05): : 789 - 802
  • [22] Microstructure and property control of hot rolled DP600 steel
    Zhou, Le-yu
    Liu, Ya-zheng
    Yang, Lian-hong
    Zhang, Dan
    ADVANCED MATERIALS, PTS 1-3, 2012, 415-417 : 938 - 942
  • [23] STUDY OF RESIDUAL STRESSES ON DP600 STEEL WELDED BY DIFFERENT PROCESSES
    Chuvas, Tatiane
    Fonseca, Maria Cindra
    IRF2016: 5TH INTERNATIONAL CONFERENCE INTEGRITY-RELIABILITY-FAILURE, 2016, : 1325 - 1326
  • [24] Failure mechanisms in DP600 steel: Initiation, evolution and fracture
    Ghadbeigi, H.
    Pinna, C.
    Celotto, S.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 588 : 420 - 431
  • [25] EBSD Characterization of Microstructure and Micro-texture in a Friction Stir-Welded DP600 Steel
    H. Ashrafi
    M. Shamanian
    M. Sanayei
    F. Farhadi
    J. A. Szpunar
    Acta Metallurgica Sinica (English Letters), 2023, 36 : 789 - 802
  • [26] Effect of Welding Parameters on the Microstructure and Tensile Properties of Friction Stir-Welded DP600 Steel
    Ashrafi, Hamid
    Shamanian, M.
    Emadi, R.
    Sarmadi, M. Ahl
    SAE INTERNATIONAL JOURNAL OF MATERIALS AND MANUFACTURING, 2019, 12 (03) : 165 - 177
  • [27] Effect of Post-Weld Heat Treatment on the Microstructure of Plasma Arc Welded DP600 Steel
    Amit A. Kuril
    M. Jagannatham
    G. D. Janaki Ram
    Srinivasa R. Bakshi
    Metallography, Microstructure, and Analysis, 2019, 8 : 848 - 860
  • [28] Effect of Post-Weld Heat Treatment on the Microstructure of Plasma Arc Welded DP600 Steel
    Kuril, Amit A.
    Jagannatham, M.
    Ram, G. D. Janaki
    Bakshi, Srinivasa R.
    METALLOGRAPHY MICROSTRUCTURE AND ANALYSIS, 2019, 8 (06) : 848 - 860
  • [29] Effects of Welding Schedules on Resistance Spot Welding of DP600 Steel
    Wan, Xiaodong
    Wang, Yuanxun
    Zhang, Peng
    ISIJ INTERNATIONAL, 2014, 54 (10) : 2375 - 2379
  • [30] Analysis of orthogonal test of properties of dual-phase DP600 steel resistance spot welded joint
    Tao, Bohao
    Li, Hong
    Song, Yonglun
    Li, Qiang
    Hanjie Xuebao/Transactions of the China Welding Institution, 2013, 34 (06): : 81 - 84
12345