Surface buffing and its effect on chloride induced SCC of 304L austenitic stainless steel

被引：3
|
作者：
Kumar, Pandu Sunil [1 ]
Acharyya, Swati Ghosh [1 ]
Rao, S. V. Ramana [2 ]
Kapoor, Komal [2 ]
机构：
[1] Univ Hyderabad, Sch Engn Sci & Technol, Hyderabad 500046, India
[2] Govt India, Dept Atom Energy, Nucl Fuel Complex, Hyderabad 500062, India
来源：
INTERNATIONAL CONFERENCE ON ADVANCES IN METALLURGY, MATERIALS AND MANUFACTURING | 2018年 / 314卷
关键词：
STRESS-CORROSION CRACKING; TRANSFORMATION;
D O I：
10.1088/1757-899X/314/1/012002
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The study focuses on the impact of buffing operation on the stress corrosion cracking (SCC) susceptibility of 304L austenitic stainless steel (SS). The SCC susceptibility of the buffed surfaces were determined by testing in boiling magnesium chloride (MgCl2) environment as per ASTM G 36. Test was conducted for 3hr, 9hr and 72hr to study the SCC susceptibility. Buffed surfaces were resistant to SCC even after 72hr of exposure to boiling MgCl2. The surface and cross section of the samples were examined for both before and after exposure to boiling MgCl2 and was characterized using optical microscopy. The study revealed that buffing operation induces compressive residual stresses on the surface, which helps in protecting the surface from SCC.
引用
收藏
页数：7
相关论文
共 50 条
  • [31] Microstructural changes in AISI 304L stainless steel due to surface machining: Effect on its susceptibility to chloride stress corrosion cracking
    Ghosh, Swati
    Kain, Vivekanand
    JOURNAL OF NUCLEAR MATERIALS, 2010, 403 (1-3) : 62 - 67
  • [32] Effect of surface damage induced by cavitation erosion on pitting and passive behaviors of 304L stainless steel
    Li, Liang
    Qiao, Yanxin
    Zhang, Lianmin
    Ma, Aili
    Daniel, Enobong Felix
    Ma, Rongyao
    Chen, Jian
    Zheng, Yugui
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2023, 30 (07) : 1338 - 1352
  • [33] Effect of surface damage induced by cavitation erosion on pitting and passive behaviors of 304L stainless steel
    Liang Li
    Yanxin Qiao
    Lianmin Zhang
    Aili Ma
    Enobong Felix Daniel
    Rongyao Ma
    Jian Chen
    Yugui Zheng
    International Journal of Minerals, Metallurgy and Materials, 2023, 30 : 1338 - 1352
  • [34] Strain-induced martensitic transformation in 304L austenitic stainless steel under ecap deformation
    Yang, Gang
    Huang, Chongxiang
    Wu, Shiding
    Zhang, Zhefeng
    Jinshu Xuebao/ Acta Metallurgica Sinica, 2009, 45 (08): : 906 - 911
  • [35] STRAIN-INDUCED MARTENSITIC TRANSFORMATION IN 304L AUSTENITIC STAINLESS STEEL UNDER ECAP DEFORMATION
    Yang Gang
    Huang Chongxiang
    Wu Shiding
    Zhang Zhefeng
    ACTA METALLURGICA SINICA, 2009, 45 (08) : 906 - 911
  • [36] Chloride induced pitting initiation on 304L stainless steel in acidic sodium sulphate solutions
    De Sa, M.S.
    Rangel, C.M.
    Sequeira, C.A.C.
    British Corrosion Journal, 1988, 23 (03): : 186 - 189
  • [37] The impact of loading rate on chloride induced stress corrosion cracking of 304L stainless steel
    Blust, Sarah M.
    Burns, James T.
    CORROSION REVIEWS, 2024, 42 (05) : 595 - 604
  • [38] Effect of Cyclic Thermal Process on Ultrafine Grain Formation in AISI 304L Austenitic Stainless Steel
    Kumar, B. Ravi
    Mahato, B.
    Sharma, Sailaja
    Sahu, J. K.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2009, 40A (13): : 3226 - 3234
  • [39] An effect of weld current and weld atmosphere on the resistance spot weldability of 304L austenitic stainless steel
    Ozyurek, Dursun
    MATERIALS & DESIGN, 2008, 29 (03) : 597 - 603
  • [40] Evolution of closure effect in short 2D cracks in a 304L austenitic stainless steel
    Vor, K.
    Gardin, C.
    Sarrazin-Baudoux, C.
    Petit, J.
    REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES, 2010, 107 (01): : 21 - 26
12345