Monitoring bending fatigue in carbon-fibre/epoxy composite strands: a comparison between mechanical and resistance techniques

被引：71
|
作者：
Weber, I
Schwartz, P
机构：
[1] Cornell Univ, Fibre Sci Program, Ithaca, NY 14853 USA
[2] Cornell Univ, Field Mech Engn, Ithaca, NY 14853 USA
来源：
COMPOSITES SCIENCE AND TECHNOLOGY | 2001年 / 61卷 / 06期
关键词：
carbon fibres; polymer-matrix composites; electrical properties; fatigue; non-destructive testing;
D O I：
10.1016/S0266-3538(01)00028-8
中图分类号：
TB33 [复合材料];
学科分类号：
摘要：
The bending fatigue behaviour of unidirectional carbon-fibre/epoxy composite strands was monitored by the changes in resistivity and in bending modulus. The fibres were PAN-based carbon fibres and the matrix was a bisphenol-A-based epoxy resin. A load cell connected to one jaw of the test assembly was used to monitor the resulting bending moment. Simultaneously the voltage, at constant current, along the longitudinal axis of the strand was measured, and a correlation between the increase in resistivity and the decrease in bending modulus was seen. (C) 2001 Elsevier Science Ltd. All rights reserved.
引用
收藏
页码：849 / 853
页数：5
相关论文
共 50 条
  • [21] Effects of voids on quasi-static and tension fatigue behaviour of carbon-fibre composite laminates
    Sisodia, Sanjay M.
    Gamstedt, E. Kristofer
    Edgren, Fredrik
    Varna, Janis
    JOURNAL OF COMPOSITE MATERIALS, 2015, 49 (17) : 2137 - 2148
  • [22] Bending Fatigue Tests of Carbon Fiber Reinforced Epoxy Resin Composite Plates
    Szuchy, Peter
    Molnar, Tamas
    Biro, Istvan
    Csikos, Sandor
    Gogolak, Laszlo
    Sarosi, Jozsef
    ACTA POLYTECHNICA HUNGARICA, 2021, 18 (02) : 199 - 213
  • [23] FATIGUE DAMAGE IN CARBON FIBRE EPOXY COMPOSITE UNDER VARIABLE LOADING CONDITIONS
    Plumtree, A.
    TMS 2014 SUPPLEMENTAL PROCEEDINGS, 2014, : 655 - 664
  • [24] Numerical analysis of unidirectional carbon-fibre/epoxy composite laminates under low velocity impacts of different forms
    Zhao, Yuting
    Zhou, Xia
    COMPUTATIONAL MATERIALS SCIENCE, 2024, 231
  • [25] Mechanical performance of carbon-fibre and glass-fibre-reinforced epoxy I-beams .2. Fractographic failure observations
    Gilchrist, MD
    Kinloch, AJ
    Matthews, FL
    COMPOSITES SCIENCE AND TECHNOLOGY, 1996, 56 (09) : 1031 - 1045
  • [26] Carbon-fibre epoxy prepreg (CFC) curing in an autoclave analogue process controlled by Dynamic Mechanical Analysis (DMA)
    Stark, W.
    Jaunich, M.
    McHugh, J.
    POLYMER TESTING, 2013, 32 (08) : 1487 - 1494
  • [27] Dynamic Mechanical Analysis (DMA) of epoxy carbon-fibre prepregs partially cured in a discontinued autoclave analogue process
    Stark, W.
    Jaunich, M.
    McHugh, J.
    POLYMER TESTING, 2015, 41 : 140 - 148
  • [28] Influence of low temperatures on the phenomenon of delamination of mode I fracture in carbon-fibre/epoxy composites under fatigue loading
    Coronado, P.
    Argueelles, A.
    Vina, J.
    Vina, I.
    COMPOSITE STRUCTURES, 2014, 112 : 188 - 193
  • [29] Mechanical behavior of carbon fibre composite rod subjected to pure bending loading
    Xie, T. Y.
    2ND INTERNATIONAL WORKSHOP ON MATERIALS SCIENCE AND MECHANICAL ENGINEERING (IWMSME2018), 2019, 504
  • [30] The effects of contamination on the mechanical properties of carbon fibre reinforced epoxy composite materials
    Zhang, M
    Mason, SE
    JOURNAL OF COMPOSITE MATERIALS, 1999, 33 (14) : 1363 - 1374
12345