Effect of Nitrogen Pressure on the Structure of Cr-N, Ta-N, Mo-N, and W-N Nanocrystals Synthesized by Arc Discharge

被引：19

作者：

Shen, Longhai ^{[1
]}

Wang, Nan ^{[1
]}

机构：

[1] Shenyang Ligong Univ, Sch Sci, Shenyang 110159, Peoples R China

来源：

JOURNAL OF NANOMATERIALS | 2011年 / 2011卷

基金：

中国国家自然科学基金;

关键词：

TUNGSTEN NITRIDE; CHROMIUM NITRIDE; MOLYBDENUM NITRIDE; DEPOSITION; STRESSES; POWDERS;

D O I：

10.1155/2011/781935

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The effect of nitrogen pressure on the structure of Ta-N, Cr-N, Mo-N, and W-N nanocrystals formed in arc discharge process was investigated. At the nitrogen pressure of 5 similar to 20 kPa, the pure cubic-phase TaN and CrN nanocrystals were formed, whereas pure cubic phase of Mo2N and W2N cannot be obtained. A little of metal Mo and a mass of metal W were mixed with the products of Mo2N and W2N, respectively. At the nitrogen pressure of 30 similar to 50 kPa, subnitride Ta2N and Cr2N and metal Cr were gradually formed in the product; furthermore, the proportion of metal Mo and W increased in the product of Mo2N and W2N, respectively. It indicated that the low nitrogen pressure makes cubic mononitride formation favorable. We explain this experimental observation in terms of the evaporation rate of anode metal and the ionization of nitrogen.

引用

页数：5

共 50 条

[41] Effect of nitrogen partial pressure on Al-Ti-N films deposited by arc ion plating
Cai, Fei
Zhang, Shihong
Li, Jinlong
Chen, Zhong
Li, Mingxi
Wang, Lei
APPLIED SURFACE SCIENCE, 2011, 258 (05) : 1819 - 1825
[42] The Influence of H, W, H/E, H3/E2, Structure and Chemical Composition on the Resistance of Ti–B–(N), Mo–B–(N), Cr–B–(N), and Zr–B–(N) Coatings to Cyclic Impact Loading
Ph. V. Kiryukhantsev-Korneev
A. D. Sytchenko
Protection of Metals and Physical Chemistry of Surfaces, 2020, 56 : 1190 - 1200
[43] The influence of nitrogen content on the microstructure and properties of W-Ta-Cr-V-N refractory high-entropy nitrides
Wang, Lingling
La, Lingmin
Zhao, Jialei
Liang, Guanjie
Yang, Zechen
Guan, Zhong
Shi, Minghui
Qin, Lin
SURFACE & COATINGS TECHNOLOGY, 2024, 494
[44] Effect of carbon content on the microstructure and mechanical properties of (Ti, W, Ta, Mo)(C, N)-(Co, Ni) cermets
Zackrisson, J
Andrén, HO
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 1999, 17 (04): : 265 - 273
[45] Effect of carbon content on the microstructure and mechanical properties of (Ti, W, Ta, Mo)(C, N)-(Co, Ni) cermets
Doktorsavh Chalmers Tek Hogsk, 1494
[46] Mo/W-N2 and -N2H2 complexes with trans nitrile ligands:: electronic structure, spectroscopic properties and relevance to nitrogen fixation
Habeck, CM
Lehnert, N
Näther, C
Tuczek, F
INORGANICA CHIMICA ACTA, 2002, 337 : 11 - 31
[47] Effect of Cerium on Structure and Properties of TiN and (Ti, Cr)N Coatings Prepared by Arc Ion Plating
徐向荣
黄拿灿
杨少敏
吴起白
Journal of Rare Earths, 2006, (S2) : 170 - 174
[48] Effect of N2 flow rate on morphology and structure of ZnO nanocrystals synthesized via vapor deposition
Chen, Z
Wu, NQ
Shan, ZW
Zhao, MH
Li, SX
Jiang, CB
Chyu, MK
Mao, SX
SCRIPTA MATERIALIA, 2005, 52 (01) : 63 - 67
[49] Synthesis of (Ti, W, Mo, Ta, Cr)(C, N) solid solution powders by carbothermal reduction-nitridation in an open system
Rong, Pengcheng
Liu, Ying
Ye, Jinwen
Cao, Qian
Liu, Anrui
JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 718 : 425 - 432
[50] Effect of nitrogen partial pressure on the structure, physical and mechanical properties of CrB2 and Cr-B-N films
Kiryukhantsev-Korneev, Ph. V.
Pierson, J. F.
Petrzhik, M. I.
Alnot, M.
Levashov, E. A.
Shtansky, D. V.
THIN SOLID FILMS, 2009, 517 (08) : 2675 - 2680

← 1 2 3 4 5 →