Regulation of growth temperature on structure, magnetism of epitaxial FeCo2O4 films

被引：2

作者：

Xie, Jingtong ^{[1
]}

Zhen, Congmian ^{[1
]}

Xu, Lei ^{[1
]}

Su, Mengyao ^{[1
]}

Pan, Chengfu ^{[1
]}

Ma, Li ^{[1
]}

Zhao, Dewei ^{[1
]}

Hou, Denglu ^{[1
]}

机构：

[1] Hebei Normal Univ, Coll Phys, Hebei Key Lab Photophys Res & Applicat, Shijiazhuang 050024, Hebei, Peoples R China

来源：

CRYSTENGCOMM | 2022年 / 24卷 / 01期

基金：

中国国家自然科学基金;

关键词：

MIXED OXIDES; SPINEL; FE; CONVERSION; CO3O4; CU;

D O I：

10.1039/d1ce00700a

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

Epitaxial FeCo2O4 films were grown by pulsed laser deposition on Al2O3 (0001) substrates at different growth temperatures in this work. The growth temperature directly affects the occupation of cations and the lattice constant, resulting in different magnetic phases and conductivity. The optimal growth temperature range was 450-550 degrees C. Double bandgaps were observed in the UV absorption spectra. Electrical measurements showed that the film grown at 450 degrees C had the lowest activation energy, and the structure of this film was more ordered. The magnetic analysis demonstrated that, in addition to the ferrimagnetic phase formed by the antiparallel arrangement of the tetrahedral and octahedral magnetic moments, there were two kinds of antiferromagnetic phases. One kind of antiferromagnetism was from the antiphase boundaries, and the other was localized antiferromagnetism at the octahedra formed by the Co2+ ions. The three kinds of magnetic phases showed different characteristics with changes in the growth temperature and measurement temperature.

引用

页码：83 / 94

页数：12

共 50 条

[31] Investigation of electrical studies of spinel FeCo2O4 synthesized by sol-gel method
Lobo, Laurel Simon
Kalainathan, S.
Kumar, A. Ruban
SUPERLATTICES AND MICROSTRUCTURES, 2015, 88 : 116 - 126
[32] Ultrasonically assisted microwave synthesis of nanostructured FeCo2O4 as potential cathode materials for supercapacitors
Salame, Paresh
Kotalgi, Karan
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2020, 31 (22) : 20072 - 20079
[33] Spinel-structured FeCo2O4 mesoporous nanosheets as efficient electrode for supercapacitor applications
Mohamed, Saad G.
Attia, Sayed Y.
Hassan, Hamdy H.
MICROPOROUS AND MESOPOROUS MATERIALS, 2017, 251 : 26 - 33
[34] Catalytic diesel soot combustion over FeCo2O4 monolithic catalysts with different morphologies
Fan, Zhenhai
Yang, Hua
Qin, Feiyang
Xiao, Jieyu
Xian, Hui
Yang, Xingchuan
Yu, Yi
Liu, Guoji
Xu, Li
Cao, Chunmei
JOURNAL OF ENVIRONMENTAL CHEMICAL ENGINEERING, 2024, 12 (03):
[35] Direct growth of FeCo2O4 nanowire arrays on flexible stainless steel mesh for high-performance asymmetric supercapacitor
Nilesh R Chodankar
Deepak P Dubal
Yongchai Kwon
Do-Heyoung Kim
NPG Asia Materials, 2017, 9 : e419 - e419
[36] Direct growth of FeCo2O4 nanowire arrays on flexible stainless steel mesh for high-performance asymmetric supercapacitor
Chodankar, Nilesh R.
Dubal, Deepak P.
Kwon, Yongchai
Kim, Do-Heyoung
NPG ASIA MATERIALS, 2017, 9 : 1 - 10
[37] Enhanced electrocatalytic activity of FeCo2O4 interfacing with CeO2 for oxygen reduction and evolution reactions
Sun, Zhihui
Cao, Xuecheng
Martinez, Ignacio G. Gonzalez
Rummeli, Mark H.
Yang, Ruizhi
ELECTROCHEMISTRY COMMUNICATIONS, 2018, 93 : 35 - 38
[38] Growth and magnetic properties of CoCr2O4 epitaxial films
Lüders, U
Sánchez, F
Fontcuberta, J
MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 2004, 109 (1-3): : 200 - 202
[39] Synthesis of multifunctional FeCo2O4 electrode using ultrasonic treatment for photocatalysis and energy storage applications
Yadav, A. A.
Hunge, Y. M.
Kulkarni, S. B.
ULTRASONICS SONOCHEMISTRY, 2019, 58
[40] Carbon Nanotube-Supported FeCo2O4 as a Catalyst for an Enhanced PMS Activation of Phenol Removal
Wang, Jing
Zhou, Huanyu
Ma, Li
Wang, Quanfeng
Sun, Da
Jin, Libo
Zeng, Guoming
Zhao, Jujiao
WATER, 2023, 15 (15)

← 1 2 3 4 5 →