DETERIORATION OF REFRACTORY CERAMIC FIBRE LINING IN AN ETHYLENE CRACKING FURNACE- A CASE STUDY

被引：0

作者：

Maity, Manabendra ^{[1
]}

Al-Zahrani, Eissa ^{[1
]}

Al-Thomali, Majed ^{[2
]}

Kareem, Mohammed Abdul ^{[2
]}

机构：

[1] Sabic Technol Ctr Jubail, Al Jubail, Saudi Arabia

[2] Eastern Petrochem Co, Al Jubail, Saudi Arabia

来源：

PROCEEDINGS OF THE UNIFIED INTERNATIONAL TECHNICAL CONFERENCE ON REFRACTORIES (UNITECR 2013) | 2014年

关键词：

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Refractory ceramic fibres (RCF) are extensively used for the lining of Ethylene cracking furnaces in the petrochemical industries. Ceramic fibre materials do normally have a tendency of deterioration (de-vitrification, shrinkage, densification, reduced fibre resiliency, reduced thermal shock resistance, etc.) after a continuous exposure to high temperature for a long time. Premature deterioration of ceramic fibre module lining was noticed in a cracking furnace. The problem was unusual and was restricted to only one of the furnaces in the plant. The root-cause of the problem was investigated by evaluating the process condition of the furnace and analyzing the ceramic fibre samples. The results revealed that the presence of alkalis (Na2O & K2O) within furnace contributed faster deterioration of ceramic fibre lining. The detailed observations and results of ceramic fibre post-mortem analysis will be discussed.

引用

页码：1105 / +

页数：3

共 25 条

[21] Simulation and Optimization of the Ethane Cracking Furnace Using ASPEN PLUS and MATLAB: A Case Study from Petrochemical Complexes
Aammer, Huda
Shakor, Zaidoon M.
Al-Sheikh, Farooq
Al-Naimi, Safa A.
Anderson, William A.
COMBUSTION SCIENCE AND TECHNOLOGY, 2023, 195 (11) : 2634 - 2654
[22] Study of dual-phase drive synchronization method and temperature measurement algorithm for measuring external surface temperatures of ethylene cracking furnace tubes
Peng, Zhiping
He, Jieguang
Tan, Yun
Cui, Delong
Li, Qirui
Qiu, Jingbo
APPLIED PETROCHEMICAL RESEARCH, 2018, 8 (03): : 163 - 172
[23] Study on the composition, microstructure and properties of new W-Al alloyed ethylene cracking furnace tube under 1100 celcius carburising test conditions
Liu, Chunjiao
Chen, Tao
Wu, Zhigang
Wang, Xinglei
Luo, Heli
Wang, Jiantao
MATERIALS AT HIGH TEMPERATURES, 2023, 40 (03) : 241 - 249
[24] A comparison of two damage models for inverse identification of mode I fracture parameters: Case study of a refractory ceramic
Samadi, Soheil
Jin, Shengli
Gruber, Dietmar
Harmuth, Harald
INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES, 2021, 197
[25] THE RELATIONSHIP BETWEEN STRUCTURAL FEATURES AND LOCAL MECHANICAL PROPERTIES OF A FINE-GRAINED MATRIX IN REFRACTORY CERAMIC MATERIALS. SiO2 CERAMICS CASE STUDY
Lapshina, A. A.
Shilko, E. V.
Buyakov, A. S.
Smolin, A. Y.
Andreev, K.
RUSSIAN PHYSICS JOURNAL, 2024, 67 (04) : 388 - 396

← 1 2 3 →