Effects of secondary orientation and temperature on the fretting fatigue behaviors of Ni-based single crystal superalloys

被引：32

作者：

Su, Yue ^{[1
]}

Han, Qi-Nan ^{[2
]}

Zhang, Cheng-Cheng ^{[3
]}

Shi, Hui-Ji ^{[1
]}

Niu, Li-Sha ^{[1
]}

Deng, Guo-Jian ^{[3
]}

Rui, Shao-Shi ^{[1
]}

机构：

[1] Tsinghua Univ, AML, Sch Aerosp Engn, Beijing 100084, Peoples R China

[2] Aircraft Strength Res Inst China, Xian 710065, Shaanxi, Peoples R China

[3] Aero Engine Grp Corp China, Shanghai Engn Res Ctr Commercial Aircraft Engine, Commercial Aircraft Engine Co Ltd, Shanghai 200241, Peoples R China

来源：

TRIBOLOGY INTERNATIONAL | 2019年 / 130卷

基金：

中国国家自然科学基金;

关键词：

Fretting fatigue; Ni-based single crystal superalloys; Secondary orientation; Temperature effect; PLASTICITY FINITE-ELEMENT; SITU SEM OBSERVATION; CRITICAL-PLANE; CYCLE FATIGUE; CRACK INITIATION; LIFE PREDICTION; DOVETAIL JOINT; NICKEL; SIMULATION; DEFORMATION;

D O I：

10.1016/j.triboint.2018.09.006

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

A dovetail fixture for fretting fatigue test was designed. Fretting fatigue experiments were performed for Nibased single crystal (NBSX) superalloys at 600 and 700 degrees C in two secondary orientations, [110] and [010]. The influence of secondary orientation and temperature on fretting fatigue behavior was investigated. The crystal plasticity finite element (CPFE) simulation was used to study the stress field at the contact region. The result indicates that the stress distribution is correlated to fretting damage, which is consistent with the crack initiation site. Fretting fatigue life is predicted based on critical plane method, which is in good agreement with the experimental result.

引用

页码：9 / 18

页数：10

共 50 条

[31] Alloying effects of refractory elements in the dislocation of Ni-based single crystal superalloys
Shiyu Ma
Jianxin Zhang
Progress in Natural Science:Materials International, 2016, 26 (06) : 636 - 642
[32] Alloying effects of refractory elements in the dislocation of Ni-based single crystal superalloys
Ma, Shiyu
Zhang, Jianxin
PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL, 2016, 26 (06) : 636 - 642
[33] Crack initiation mechanisms during very high cycle fatigue of Ni-based single crystal superalloys at high temperature
Cervellon, A.
Hemery, S.
Kuernsteiner, P.
Gault, B.
Kontis, P.
Cormier, J.
ACTA MATERIALIA, 2020, 188 (188) : 131 - 144
[34] Investigations on the thermo-mechanical fatigue of two Ni-based single-crystal superalloys
Zhou, H
Harada, H
Ro, Y
Okada, I
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 394 (1-2): : 161 - 167
[35] Low Cycle Fatigue Failure Analysis of a Ni-Based Single Crystal Superalloys at 850 °C
Zhang, Xuhui
Gao, Hangshan
Wen, Zhixun
Zhang, Haocheng
Yue, Zhufeng
ADVANCED ENGINEERING MATERIALS, 2019, 21 (02)
[36] A comparative study of thermo-mechanical fatigue of two Ni-based single crystal superalloys
Zhou, H
Osawa, M
Harda, H
Yokokawa, T
Koizumi, Y
Kobayashi, I
Waki, M
Ro, Y
Okada, I
SUPERALLOYS 2004, 2004, : 225 - 231
[37] A review of composition evolution in Ni-based single crystal superalloys
Wanshun Xia
Xinbao Zhao
Liang Yue
Ze Zhang
Journal of Materials Science & Technology, 2020, 44 (09) : 76 - 95
[38] Characterization and formation of σ/γ interface in Ni-based single crystal superalloys
Ma, Shiyu
Zhang, Jianxin
Li, Xueqiao
Mao, Shengcheng
MATERIALS RESEARCH EXPRESS, 2017, 4 (11):
[39] Unveiling the Re effect in Ni-based single crystal superalloys
Wu, Xiaoxiang
Makineni, Surendra Kumar
Liebscher, Christian H.
Dehm, Gerhard
Mianroodi, Jaber Rezaei
Shanthraj, Pratheek
Svendsen, Bob
Buerger, David
Eggeler, Gunther
Raabe, Dierk
Gault, Baptiste
NATURE COMMUNICATIONS, 2020, 11 (01)
[40] A review of composition evolution in Ni-based single crystal superalloys
Xia, Wanshun
Zhao, Xinbao
Yue, Liang
Zhang, Ze
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2020, 44 : 76 - 95

← 1 2 3 4 5 →