Electron microscopic and metallographical investigations on superconducting MgB2 tapes with mechanically alloyed precursor powder

被引：0
|
作者：
Schubert, Margitta
Hassler, Wolfgang [1 ]
Rodig, Christian [1 ]
Herrmann, Marlco [1 ]
Schroeder, Kerstin
Holzapfel, Bernhard [1 ]
Schultz, Ludwig [1 ]
机构：
[1] Leibniz Inst Festkorper & Werkstoffforsch Dresden, D-01171 Dresden, Germany
来源：
PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY | 2007年 / 44卷 / 12期
关键词：
D O I：
10.3139/147.100365
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Magnesium diboride is a cost-efficient superconducting material with a transition temperature of 40 K. Technical conductors as wires or tapes were prepared as composite of the ceramic superconductor and a metallic sheath using the powder-in-tube (PIT)-technology. High energy milled powder consisting of Mg, B and partially reacted MgB2 is used as precursor. Metallographical and electron microscope (SEM) investigations at tapes prepared with different precursor powders or sheath materials contribute to optimize the conductors and to draw conclusions for the processing of the tapes. Optimized tapes are characterized by a critical current density of 10(4) A/cm(2) at 4.2 K and 10 T.
引用
收藏
页码：566 / 578
页数：13
相关论文
共 50 条
  • [31] Superconducting properties of powder-in-tube MgB2 tapes without and withWSi2 addition
    Ma, YW
    Kumakura, H
    Matsumoto, A
    Takeya, H
    Togano, K
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2004, 408 : 138 - 139
  • [32] Correlation of superconducting properties and microstructure of MgB2 wires and tapes
    Birajdar, B.
    Eibl, O.
    Braccini, V.
    Grasso, G.
    Pachla, W.
    Herrman, M.
    Haessler, W.
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2007, 460 (1409-1410): : 1409 - 1410
  • [33] Effect of fabrication process on the superconducting properties of MgB2 tapes
    Zhang, X. P.
    Ma, Y. W.
    Wang, D. L.
    Gao, Z. S.
    Wang, L.
    Watanabe, K.
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2008, 468 (15-20): : 1809 - 1812
  • [34] Superconducting Properties and Microstructure in MgB2 Bulks, Wires and Tapes
    冯勇
    阎果
    赵勇
    吴晓京
    周廉
    张平祥
    Tsinghua Science and Technology, 2003, (03) : 316 - 333
  • [35] Influence of MgB2 powder quality on the transport properties of Cu-sheathed MgB2 tapes
    Fujii, H
    Kumakura, H
    Togano, K
    PHYSICA C, 2001, 363 (04): : 237 - 242
  • [36] Mechanically reinforced MgB2 wires and tapes with high transport currents
    Nast, R
    Schlachter, SI
    Zimmer, S
    Reiner, H
    Goldacker, W
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2002, 372 : 1241 - 1244
  • [37] The improvement of in-situ powder in tube MgB2 tapes by mixing MgB2 to the starting powder of MgH2 and B
    Nakane, T
    Fujii, H
    Matsumoto, A
    Kitaguchi, H
    Kumakura, H
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2005, 426 : 1238 - 1243
  • [38] Strong influence of precursor powder on the critical current density of Fe-sheathed MgB2 tapes
    Wang, Dongliang
    Ma, Yanwei
    Yu, Zhengguang
    Gao, Zhaoshun
    Zhang, Xianping
    Watanabe, K.
    Mossang, E.
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2007, 20 (06): : 574 - 578
  • [39] Superconducting properties of aromatic hydrocarbon-added powder-in-tube MgB2/Fe tapes
    Yamada, H.
    Uchiyama, N.
    Kumakura, H.
    Kitaguchi, H.
    Matsumoto, A.
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2007, 17 (02) : 2850 - 2853
  • [40] Microstructure and impurity dependence in mechanically alloyed nanocrystalline MgB2 superconductors
    Perner, O
    Eckert, J
    Hässler, W
    Fischer, C
    Müller, KH
    Fuchs, G
    Holzapfel, B
    Schultz, L
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2004, 17 (10): : 1148 - 1153
12345