Synthesis and Erosion Behaviors of Nanoscale Coatings Prepared by Wire Arc Spraying

被引：0
|
作者：
Cheng, J. B. [1 ,2 ]
Xiang, X. B. [2 ]
Wang, Z. H. [1 ]
Xu, B. S. [2 ]
机构：
[1] Hohai Univ, Coll Mech & Mat, Nanjing 210098, Jiangsu, Peoples R China
[2] Natl Key Lab Remfg, Beijing 100072, Peoples R China
来源：
RARE METAL MATERIALS AND ENGINEERING | 2012年 / 41卷
关键词：
coatings; nano materials; abrasive; THERMAL SPRAY; TEMPERATURES; VELOCITY; ALLOYS; STEEL;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effects of erosive parameters, such as impact angles and environment temperature, on erosion properties of FeBSiCrMnNb nanoscale coatings were investigated. A series of coatings were prepared by wire arc spraying process. The microstructure of the coating consists of amorphous and alpha (Fe,Cr) nanocrystalline phase. The nanocrystals with average size of 39 nm are homogenously dispersed in amorphous matrix. The erosion results reveal that the coating exhibits better erosion resistance at lower impact angle. The erosion rates of the coating decrease as function of environment temperature. The relatively erosion resistance of the nanoscale coating is 3.7 times higher than that of AISI1045 steel substrate at 650 degrees C. The main failure mechanism of the coating is brittle fracture.
引用
收藏
页码：144 / 147
页数：4
相关论文
共 50 条
  • [31] Electrical Resistivity of Wire Arc Sprayed Zn and Cu Coatings for In-Mold-Metal-Spraying
    Bobzin, K.
    Oete, M.
    Knoch, M. A.
    Liao, X.
    Hopmann, Ch
    Ochotta, P.
    20TH CHEMNITZ SEMINAR ON MATERIALS ENGINEERING, 2018, 373
  • [32] Laser surface texturing to enhance adhesion bond strength of spray coatings - Cold spraying, wire-arc spraying, and atmospheric plasma spraying
    Kromer, R.
    Costil, S.
    Verdy, C.
    Gojon, S.
    Liao, H.
    SURFACE & COATINGS TECHNOLOGY, 2018, 352 : 642 - 653
  • [33] Corrosion behaviors of arc spraying single and double layer coatings in simulated Dagang soil solution
    林碧兰
    路新瀛
    李龙
    TransactionsofNonferrousMetalsSocietyofChina, 2009, 19 (06) : 1556 - 1561
  • [34] Corrosion behaviors of arc spraying single and double layer coatings in simulated Dagang soil solution
    Lin Bi-lan
    Lu Xin-ying
    Li Long
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2009, 19 (06) : 1556 - 1561
  • [35] Erosion and corrosion behaviors of ADI deposited TiN/TiAIN coatings by cathodic arc evaporation
    Hsu, CH
    Lu, JK
    Lai, KL
    Chen, ML
    MATERIALS TRANSACTIONS, 2005, 46 (06) : 1417 - 1424
  • [36] High-Temperature Erosion Resistance of FeBSiNb Amorphous Coatings Deposited by Arc Spraying for Boiler Applications
    Cheng, J. B.
    Liang, X. B.
    Chen, Y. X.
    Wang, Z. H.
    Xu, B. S.
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2013, 22 (05) : 820 - 827
  • [37] Microstructure and high temperature erosion-wear performance of coatings produced by arc spraying core wires
    College of Mechanical and Electronic Engineering, China University of Petroleum, Dongying 257061, China
    Zhongguo Shiyou Daxue Xuebao (Ziran Kexue Ban), 2009, 2 (122-126):
  • [38] High-Temperature Erosion Resistance of FeBSiNb Amorphous Coatings Deposited by Arc Spraying for Boiler Applications
    J. B. Cheng
    X. B. Liang
    Y. X. Chen
    Z. H. Wang
    B. S. Xu
    Journal of Thermal Spray Technology, 2013, 22 : 820 - 827
  • [39] MICROSTRUCTURAL CHARACTERIZATION OF Ni-5Al COATINGS DEPOSITED BY ELECTRIC ARC WIRE THERMAL SPRAYING
    Axente, Mariana
    Geaman, Virgil
    MODTECH 2011: NEW FACE OF T.M.C.R., VOL I AND II, 2011, : 41 - 44
  • [40] CHARACTERIZATION OF Ni-5Al AND SPRASTEEL COATINGS DEPOSITED BY ELECTRIC ARC WIRE THERMAL SPRAYING
    Axente, Mariana
    Geaman, Virgil
    METALURGIA INTERNATIONAL, 2011, 16 (05): : 89 - 92
12345