Effect of bolt tightening on the fatigue behavior of GLARE double shear lap joints

被引：0
|
作者：
Abazadeh, B. [1 ]
Maleki, Hr [1 ]
机构：
[1] Univ Bonab, Fac Mech Engn, Bonab, Iran
来源：
JOURNAL OF COMPOSITE MATERIALS | 2021年 / 55卷 / 21期
关键词：
Bolt clamping; fatigue; GLARE; fiber metal laminate; pre-stress; CRACK GROWTH-BEHAVIOR; FAILURE ANALYSIS; CLAMPING FORCE; FIBER; 2024-T3; DAMAGE; MODEL;
D O I：
10.1177/00219983211003315
中图分类号：
TB33 [复合材料];
学科分类号：
摘要：
In this paper, the effect of bolt torque tightening has been investigated on the fatigue behavior of GLARE in double shear lap configuration. To do so, experimental fatigue tests were conducted using GLARE3-5/4-0.4 specimens with applied torques of 0 (finger tightened), 2 and 4 Nm at different cyclic longitudinal load ranges to achieve the stress-life (S-N) curves. The results revealed that applying and increasing the clamping force enhances the fatigue life of the GLARE specimens. Furthermore, comparison of fatigue test results of GLARE and available monolithic aluminum alloy 2024-T3 plates indicated when the applied load range is low, the effect of clamping force is more noticeable in GLARE specimens due to longer fatigue crack growth life of GLARE. Also, the occurrence of fretting fatigue didn't reduce the fatigue life of GLARE specimens considerably in contrary to aluminum sheets because of the laminated structure of GLARE. The obtained results can provide insights in designing bolted GLARE joints with superior fatigue in-service performance.
引用
收藏
页码：2911 / 2920
页数：10
相关论文
共 50 条
  • [31] Evaluation of the Effect of Tightening Torque on Single-lap Bolted Joints
    Boualamallah, Djamal
    Ghazi, Abdelkader
    Miloudi, Abdelkader
    Merzoug, Mohamed
    ENGINEERING TECHNOLOGY & APPLIED SCIENCE RESEARCH, 2022, 12 (01) : 8123 - 8128
  • [32] Revealing the competitive fatigue failure behaviour of CFRP-aluminum two-bolt, double-lap joints
    Shan, Meijuan
    Zhao, Libin
    Liu, Fengrui
    Qi, Dexuan
    Zhang, Jianyu
    COMPOSITE STRUCTURES, 2020, 244
  • [33] EFFECT OF WASHERS AND BOLT TENSION ON THE BEHAVIOR OF DOUBLE-LAP S2-GLASS FABRIC-EPOXY COMPOSITE JOINTS
    Virupaksha, Vinayshankar L.
    Nassar, Sayed A.
    PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, VOL 3, 2009, : 609 - 618
  • [34] Effect of torque tightening on the fatigue strength of bolted joints
    Minguez, Jose Maria
    Vogwell, Jeffrey
    ENGINEERING FAILURE ANALYSIS, 2006, 13 (08) : 1410 - 1421
  • [35] Experimental Investigations on the Effects of Torque Tightening on the Fatigue Strength of Double-lap Simple Bolted and Hybrid (Bolted/Bonded) Joints
    Esmaeili, F.
    Zehsaz, M.
    Chakherlou, T. N.
    STRAIN, 2014, 50 (04): : 347 - 354
  • [36] Fatigue behavior of single lap adhesive composite joints
    Saunders, I
    Dzenis, YA
    RECENT DEVELOPMENTS IN DURABILITY ANALYSIS OF COMPOSITE SYSTEMS, 2000, : 127 - 131
  • [37] Reasons for different fatigue lives of riveted double-shear lap joints manufactured by two producers
    Papuga, Jan
    Stejskal, Jiri
    ENGINEERING FAILURE ANALYSIS, 2023, 150
  • [38] Effects of bolt torque tightening on the strength and fatigue life of airframe FRP laminate bolted joints
    Giannopoulos, Ioannis K.
    Doroni-Dawes, Damian
    Kourousis, Kyriakos I.
    Yasaee, Mehdi
    COMPOSITES PART B-ENGINEERING, 2017, 125 : 19 - 26
  • [39] Effect of the surface morphology over the fatigue performance of metallic single lap-shear joints
    Moroni, F.
    Musiari, F.
    Favi, C.
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2020, 97
  • [40] The Effect of Viscoelasticity on Creep Behavior of Double-Lap Adhesively Bonded Joints
    Reza, Arash
    Shishesaz, Mohammad
    Naderan-Tahan, Khosro
    LATIN AMERICAN JOURNAL OF SOLIDS AND STRUCTURES, 2014, 11 (01): : 35 - 50
12345