The corrosion morphology and crack growth analysis of aluminum alloy

被引：0
|
作者：
Mu, Zhitao [1 ]
Liu, Hui [2 ]
Zhu, Zuotao [2 ]
Chen, Dinghai [2 ]
机构：
[1] Naval Aeronaut Engn Acad, Dept Aeronaut Mech, Qingdao Branch, Qingdao 266041, Peoples R China
[2] Naval Aeronaut Engn Acad, Qingdao Branch, Qingdao 266041, Peoples R China
来源：
INFORMATION ENGINEERING FOR MECHANICS AND MATERIALS SCIENCE, PTS 1 AND 2 | 2011年 / 80-81卷
关键词：
corrosion pits; corrosion morphology; fatigue life; fatigue crack; crack growth;
D O I：
10.4028/www.scientific.net/AMM.80-81.464
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The relation between corrosion depth and width with corrosion time is according with the power function. The corrosion pits can be seen as ellipse balls through the examination of QUESTAR three-dimensional optics microscope. Corrosion can decrease the fatigue life of materials and is the main reason of fatigue crack form and grow; through AFGROW analyze we can see that the AFGROW software can simulate crack growth life well and the error is low, the crack growth life and critical crack length are conservative than experiment values.
引用
收藏
页码：464 / +
页数：2
相关论文
共 50 条
  • [21] Scaling invariance of fatigue crack growth in aluminum alloy
    Oborin, Vladimir
    Naimark, Oleg
    20TH EUROPEAN CONFERENCE ON FRACTURE, 2014, 3 : 1004 - 1008
  • [22] Corrosion fatigue crack propagation of an aluminum alloy under periodic overloads
    Wang, R.
    Zheng, X.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2012, 35 (05) : 389 - 398
  • [23] STRESS-CORROSION CRACK GROWTH IN ALUMINUM-ALLOYS
    THEOCARIS, PS
    PAPADOPOULOS, GA
    ENGINEERING FRACTURE MECHANICS, 1977, 9 (04) : 781 - &
  • [24] Fatigue crack nucleation and small crack growth in an extruded 6061 aluminum alloy
    McCullough, R. R.
    Jordon, J. B.
    Allison, P. G.
    Rushing, T.
    Garcia, L.
    INTERNATIONAL JOURNAL OF FATIGUE, 2019, 119 : 52 - 61
  • [25] Transition from pitting to fatigue crack growth - Modeling of corrosion fatigue crack nucleation in a 2024-T3 aluminum alloy
    Chen, GS
    Wan, KC
    Gao, M
    Wei, RP
    Flournoy, TH
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1996, 219 (1-2): : 126 - 132
  • [26] Corrosion fatigue crack growth of 7475 T7351 aluminum alloy under flight simulation loading
    Chemin, A.
    Spinelli, D.
    Bose, W. Filho
    Ruchert, C.
    3RD INTERNATIONAL CONFERENCE ON MATERIAL AND COMPONENT PERFORMANCE UNDER VARIABLE AMPLITUDE LOADING, VAL 2015, 2015, 101 : 85 - 92
  • [27] Effects of precrack environment on subsequent corrosion fatigue crack growth behavior of a squeeze-cast aluminum alloy
    Shiozawa, Kazuaki
    Sun, Shuming
    Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science, 1995, 26 A (11): : 3049 - 3051
  • [28] Electrochemical noise analysis on corrosion of aluminum alloy
    Tian, Zhiqiang
    Kong, Xiaodong
    Wu, Gang
    Wang, Yuansheng
    ADVANCES IN SUPERALLOYS, PTS 1 AND 2, 2011, 146-147 : 1043 - 1048
  • [29] Effect of Alternate Corrosion and Fatigue on Fatigue Crack Growth Characterization of 2024-T4 Aluminum Alloy
    Zhang, Tianyu
    He, Yuting
    Li, Changfan
    Zhang, Teng
    Zhang, Sheng
    MATHEMATICAL PROBLEMS IN ENGINEERING, 2020, 2020 (2020)
  • [30] Study on Crack Initiation and Propagation of New Corrosion Inhibitor during Stress Corrosion of Aluminum Alloy
    Du, Juan
    Wei, Zi-ming
    Yang, Xu-dong
    Liu, Qing-mao
    Song, Hai-peng
    Hu, Xue-lan
    Li, Xiang-yun
    JOURNAL OF SPECTROSCOPY, 2020, 2020
12345