The corrosion morphology and crack growth analysis of aluminum alloy

被引：0
|
作者：
Mu, Zhitao [1 ]
Liu, Hui [2 ]
Zhu, Zuotao [2 ]
Chen, Dinghai [2 ]
机构：
[1] Naval Aeronaut Engn Acad, Dept Aeronaut Mech, Qingdao Branch, Qingdao 266041, Peoples R China
[2] Naval Aeronaut Engn Acad, Qingdao Branch, Qingdao 266041, Peoples R China
来源：
INFORMATION ENGINEERING FOR MECHANICS AND MATERIALS SCIENCE, PTS 1 AND 2 | 2011年 / 80-81卷
关键词：
corrosion pits; corrosion morphology; fatigue life; fatigue crack; crack growth;
D O I：
10.4028/www.scientific.net/AMM.80-81.464
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The relation between corrosion depth and width with corrosion time is according with the power function. The corrosion pits can be seen as ellipse balls through the examination of QUESTAR three-dimensional optics microscope. Corrosion can decrease the fatigue life of materials and is the main reason of fatigue crack form and grow; through AFGROW analyze we can see that the AFGROW software can simulate crack growth life well and the error is low, the crack growth life and critical crack length are conservative than experiment values.
引用
收藏
页码：464 / +
页数：2
相关论文
共 50 条
  • [1] Investigation on corrosion fatigue crack growth rate in 7075 aluminum alloy
    Meng, Xiangqi
    Lin, Zhuoying
    Wang, Feifei
    MATERIALS & DESIGN, 2013, 51 : 683 - 687
  • [2] Reliability analysis of corrosion fatigue crack growth for 2024-T3 aluminum alloy
    Ge, S.
    Li, Z.
    Zhang, J. G.
    Xiao, Y. C.
    Liu, G. Q.
    Bao, B. S.
    MATERIALS AND PRODUCT TECHNOLOGIES, 2008, 44-46 : 105 - 110
  • [3] EFFECTS OF RESIDUAL STRESSES ON STRESS CORROSION CRACK GROWTH RATES IN ALUMINUM ALLOY
    HYATT, MV
    CORROSION, 1970, 26 (12) : 547 - &
  • [4] CREEP CRACK GROWTH FRACTURE MORPHOLOGY OF IN-9021 ALUMINUM ALLOY.
    Shaw, W.J.D.
    Metallography, 1986, 19 (03): : 335 - 343
  • [5] Propagation of corrosion induced fatigue crack in aluminum alloy
    Kumar, Pawan
    Verma, B. B.
    AIMS MATERIALS SCIENCE, 2022, 9 (03) : 512 - 521
  • [6] CREEP CRACK-GROWTH FRACTURE MORPHOLOGY OF IN-9021 ALUMINUM-ALLOY
    SHAW, WJD
    METALLOGRAPHY, 1986, 19 (03): : 335 - 343
  • [7] EBSD analysis of fatigue crack growth of 2124 aluminum alloy for aviation
    Jian, Haigen
    Yin, Zhimin
    Jiang, Feng
    Li, Xue
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2014, 43 (06): : 1332 - 1336
  • [8] Analysis of 7050 Aluminum Alloy Crack Growth by Laser Shock Processing
    Ren, X. D.
    Zhang, T.
    Zhang, Y. K.
    Jiang, D. W.
    Chen, K. M.
    MANUFACTURING SCIENCE AND ENGINEERING, PTS 1-5, 2010, 97-101 : 3852 - 3856
  • [9] EBSD Analysis of Fatigue Crack Growth of 2124 Aluminum Alloy for Aviation
    Jian Haigen
    Yin Zhimin
    Jiang Feng
    Li Xue
    RARE METAL MATERIALS AND ENGINEERING, 2014, 43 (06) : 1332 - 1336
  • [10] Corrosion Fatigue Crack Growth in Alloy 690
    Chen Kai
    Du Donghai
    Lu Hui
    Zhang Lefu
    RARE METAL MATERIALS AND ENGINEERING, 2017, 46 (08) : 2130 - 2136
12345