A stiffness degradation model for composite laminates under fatigue loading

被引：122

作者：

Whitworth, HA ^{[1
]}

机构：

[1] Howard Univ, Dept Engn Mech, Washington, DC 20059 USA

来源：

COMPOSITE STRUCTURES | 1997年 / 40卷 / 02期

关键词：

D O I：

10.1016/S0263-8223(97)00142-6

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

An investigation has been conducted for the purpose of evaluating the stiffness degradation of composite laminates during fatigue loading. Based on this investigation, a model is proposed that is capable of predicting the stiffness degradation in composite laminates. This model is based on an assumed relationship between the failure stiffness and the applied stress. An experimental program comprised of a number of static and fatigue tests using coupon specimens of graphite/epoxy [+/-35](2S) laminates was carried out for the purpose of evaluating the model. (C) 1998 Elsevier Science Ltd. All rights reserved.

引用

页码：95 / 101

页数：7

共 50 条

[21] A simplified micromechanics model for predicting the stiffness degradation in symmetric composite laminates
Farrokhabadi, A.
Mohammadi, B.
Hosseini-Toudeshky, H.
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2015, 38 (11) : 1334 - 1346
[22] A Residual Stiffness-Residual Strength Coupled Model for Composite Laminate Under Fatigue Loading
Lian, W.
FATIGUE BEHAVIOUR OF FIBER REINFORCED POLYMERS: EXPERIMENTS AND SIMULATIONS, 2012, : 15 - 31
[23] Probabilistic strength based matrix crack evolution model in multidirectional composite laminates under fatigue loading
Jagannathan, N.
Gururaja, S.
Manjunatha, C. M.
INTERNATIONAL JOURNAL OF FATIGUE, 2018, 117 : 135 - 147
[24] A damage model for matrix cracks in composite laminates under fatigue loading based on continuum damage mechanics
Qi, Wenxuan
Huang, Jie
Yao, Weixing
Shen, Haojie
INTERNATIONAL JOURNAL OF FATIGUE, 2024, 184
[25] Comparison of damage mechanisms in curved composite laminates under static and fatigue loading
Tasdemir, B.
Coker, D.
COMPOSITE STRUCTURES, 2019, 213 : 190 - 203
[26] DELAMINATION FORMATION AND DELAMINATION PROPAGATION OF COMPOSITE LAMINATES UNDER COMPRESSIVE FATIGUE LOADING
熊峻江
Chinese Journal of Aeronautics, 2000, (01) : 8 - 13
[27] Prediction of fatigue damage and life for composite laminates under service loading spectra
Lee, LJ
Fu, KE
Yang, JN
COMPOSITES SCIENCE AND TECHNOLOGY, 1996, 56 (06) : 635 - 648
[28] Damage Progression in Thick Curved Composite Laminates under Static and Fatigue Loading
Tasdemir, B.
Coker, D.
SCIENCE OF MAKING TORQUE FROM WIND (TORQUE 2018), 2018, 1037
[29] Mixed mode delamination growth of multidirectional composite laminates under fatigue loading
Peng, Lei
Xu, Jifeng
Zhang, Jianyu
Zhao, Libin
ENGINEERING FRACTURE MECHANICS, 2012, 96 : 676 - 686
[30] Mode I delamination growth of multidirectional composite laminates under fatigue loading
Peng, Lei
Zhang, Jianyu
Zhao, Libin
Bao, Rui
Yang, Hongqin
Fei, Binjun
JOURNAL OF COMPOSITE MATERIALS, 2011, 45 (10) : 1077 - 1090

← 1 2 3 4 5 →