Magnetization Studies on Tb-Fe and Tb-Fe-Co Thin Films

被引：0

作者：

Rajasekhar, P. ^{[1
]}

Markandeyulu, G. ^{[1
]}

机构：

[1] IIT Madras, Dept Phys, Adv Magnet Mat Lab, Chennai 600036, India

来源：

IEEE TRANSACTIONS ON MAGNETICS | 2019年 / 55卷 / 02期

关键词：

Easy magnetization direction (EMD); magnetization; perpendicular magnetic anisotropy (PMA); rare-earth (R)-transition (T) metal intermetallics; Tb-Fe and Tb-Fe-Co thin films; ANISOTROPY; IRON;

D O I：

10.1109/TMAG.2018.2878087

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

Magnetization studies were carried out on Tb-Fe and Tb-Fe-Co thin films, prepared using magnetron co-sputtering technique. The films Tb25Fe75 and Tb31Fe69 were found to have perpendicular magnetic anisotropy (PMA) both at 25 and 300 K. In Tb-Fe-Co films, all the films were observed to exhibit planar anisotropy at 25 K, due to the increase of strain-induced anisotropy as a result of large magnetostriction at low temperatures leading to the development of in-plane anisotropy. PMA was observed in the films Tb35Fe37Co28, Tb56Fe25Co19, and Tb63Fe20Co17 at 300 K. The Curie temperatures (T-C) of both TbxFe100-x and Tb-Fe-Co films were found to be above room temperature (RT). Observing the Curie temperatures well above the RT, with the existence of PMA at RTs, is an interesting object in these films to find in magnetic data storage applications.

引用

页数：4

共 50 条

[31] THE EFFECT OF (TB-FE) THICKNESS ON THE RESISTIVITY AND MAGNETORESISTANCE OF (TB-FE)/PT MULTILAYERS
NIGAM, AK
ACHARYA, BR
PRASAD, S
CHANDRA, G
VENKATARAMANI, N
KRISHNAN, R
[J]. JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1995, 148 (1-2) : 339 - 341
[32] Understanding thickness dependent magnetic properties of Tb-Fe thin films
Basumatary, Himalay
Chelvane, J. Arout
Rao, D. V. Sridhara
Talapatra, A.
Mohanty, J.
Kumar, Deepak
Singh, Vajinder
Kamat, S., V
Ranjan, Rajeev
[J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2021, 869 (869)
[33] Temperature dependence of activation volumes in Tb-Fe-Co magneto-optic thin films
Thomson, T
OGrady, K
[J]. IEEE TRANSACTIONS ON MAGNETICS, 1997, 33 (01) : 795 - 798
[34] Dependence of all-optical magnetic switching on the sublattice magnetization orientation in Tb-Fe thin films
Hassdenteufel, A.
Schubert, C.
Schmidt, J.
Richter, P.
Zahn, D. R. T.
Salvan, G.
Helm, M.
Bratschitsch, R.
Albrecht, M.
[J]. APPLIED PHYSICS LETTERS, 2014, 105 (11)
[35] Effect of anisotropy on anomalous Hall effect in Tb-Fe thin films
Babu, V. Hari
Markandeyulu, G.
Subrahmanyam, A.
[J]. JOURNAL OF APPLIED PHYSICS, 2009, 105 (11)
[36] Investigation of magnetization reversal mechanism in nanometer-thick Tb-Fe-Co films with Al overlayer
Ito, H
[J]. IEEE TRANSACTIONS ON MAGNETICS, 1996, 32 (05) : 4800 - 4802
[37] Temperature dependence of activation volumes in Tb-Fe-Co magneto-optic thin films
Thomson, T.
O'Grady, K.
[J]. IEEE Transactions on Magnetics, 1997, 33 (1 pt 2): : 795 - 798
[38] INTRINSIC ANISOTROPY OF TB-FE FILMS PREPARED BY MAGNETRON CO SPUTTERING
VANDOVER, RB
HONG, M
GYORGY, EM
DILLON, JF
ALBISTON, SD
[J]. JOURNAL OF APPLIED PHYSICS, 1985, 57 (08) : 3897 - 3899
[39] Diffusion of Co-57 in amorphous Tb-Fe and Tb-Fe-Si alloys
Yamada, K
Iijima, Y
Fukamichi, K
[J]. DEFECT AND DIFFUSION FORUM/JOURNAL, 1997, 143 : 765 - 770
[40] MAGNETIC-ANISOTROPY AND OTHER STUDIES IN AMORPHOUS TB-FE FILMS
KRISHNAN, R
PORTE, M
TESSIER, M
VITTON, JP
LECARS, Y
[J]. IEEE TRANSACTIONS ON MAGNETICS, 1988, 24 (02) : 1773 - 1777

← 1 2 3 4 5 →