STUDY ON THE STABILITY OF RETAINED AUSTENITE IN MARINE STEEL

被引：0
|
作者：
He, X. Z. [1 ]
Li, J. G. [1 ]
Yan, L. [2 ]
Zhang, X. Y. [1 ]
机构：
[1] Univ Sci & Technol Liaoning, Anshan, Peoples R China
[2] Ansteel Grp Res Inst, State Key Lab Met Mat Marine Equipment & Applicat, Beijing, Peoples R China
来源：
METALURGIJA | 2020年 / 59卷 / 02期
关键词：
marine steel; heat treatment; microstructure; retained austenite; mechanical stability;
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The residual arastenite stability in marine steel was studied by different heat treatment processes. After heat-treatment process 1 (quenching + tempering) and heat treatment process 2 (quenching + intercritical annealing + tempering), the austenite content was determined by X-ray diffraction(XRD), and the microstructure of the test steel was tested by Scanning electron microscope(SEM),Transmission electron microscope(TEM), and Electron Backscattered Diffraction(EBSD). Experimental results showed that the microstructure of the test steel consisted of martensite/bainite + ferrite + retained austenite. The retained austenite volume fractions were 20,8 % and 18,1 %, spectively, for process 1 and process 2.The retained arastenite morphology, C content,distribution, and grain size all affect a steel's thermal and mechanical stability. Film-like residual austenite with high C content and fine grain size has the best stability.
引用
收藏
页码：159 / 162
页数：4
相关论文
共 50 条
  • [1] Thermal stability of retained austenite in bainitic steel: an in situ study
    Podder, A. Saha
    Lonardelli, I.
    Molinari, A.
    Bhadeshia, H. K. D. H.
    PROCEEDINGS OF THE ROYAL SOCIETY A-MATHEMATICAL PHYSICAL AND ENGINEERING SCIENCES, 2011, 467 (2135): : 3141 - 3156
  • [2] Stability of retained austenite in quenching and partitioning steel
    Ju, Xin-Hua, 1600, Editorial Office of Transactions of Materials and Heat Treatment (35):
  • [3] On the thermodynamic stability of retained austenite in 4340 steel
    Haidemenopoulos, GN
    Vasilakos, AN
    JOURNAL OF ALLOYS AND COMPOUNDS, 1997, 247 : 128 - 133
  • [4] Optimizing the Morphology and Stability of Retained Austenite in a δ-TRIP Steel
    H. L. Yi
    P. Chen
    H. K. D. H. Bhadeshia
    Metallurgical and Materials Transactions A, 2014, 45 : 3512 - 3518
  • [5] Retained austenite thermal stability in a nanostructured bainitic steel
    Avishan, Behzad
    Garcia-Mateo, Carlos
    Yazdani, Sasan
    Caballero, Francisca G.
    MATERIALS CHARACTERIZATION, 2013, 81 : 105 - 110
  • [6] Optimizing the Morphology and Stability of Retained Austenite in a δ-TRIP Steel
    Yi, H. L.
    Chen, P.
    Bhadeshia, H. K. D. H.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2014, 45A (08): : 3512 - 3518
  • [7] Investigation of retained austenite and its stability in TRIP steel
    National Engineering Research Center for Advanced Rolling Technology, University of Science and Technology Beijing, Beijing 100083, China
    不详
    Kang T'ieh, 2007, 8 (60-63+82):
  • [8] THE STABILITY OF RETAINED AUSTENITE IN 9NI STEEL
    KIM, JI
    FULTZ, B
    KIM, YH
    MORRIS, JW
    JOURNAL OF METALS, 1983, 35 (12): : 46 - 46
  • [9] STUDY OF THE STEEL SHEET CONTAINING RETAINED AUSTENITE .2. THE EFFECT OF RETAINED AUSTENITE ON THE DUCTILITY OF STEEL SHEETS
    MATSUMURA, O
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 71 : 1293 - 1293
  • [10] INFLUENCE OF RETAINED AUSTENITE ON THE BENDING FORMABILITY OF STEEL SHEETS (STUDY OF THE STEEL SHEET CONTAINING RETAINED AUSTENITE - VIII).
    Sakuma, Yasuharu
    Matsumura, Osamu
    Takechi, Hiroshi
    Ishii, Yoshio
    Usuda, Matsuo
    Transactions of the Iron and Steel Institute of Japan, 1987, 28 (01)
12345