Corrosion resistance of CrN and CrCN/CrN coatings deposited using cathodic arc evaporation in Ringer's and Hank's solutions

被引：68
|
作者：
Gilewicz, A. [1 ]
Chmielewska, P. [1 ]
Murzynski, D. [1 ]
Dobruchowska, E. [1 ]
Warcholinski, B. [1 ]
机构：
[1] Koszalin Univ Technol, Fac Technol & Educ, Koszalin, Poland
来源：
SURFACE & COATINGS TECHNOLOGY | 2016年 / 299卷
关键词：
Corrosion; CrN; CrCN/CrN; Tafel curves; Ringer's solution; Hank's solution; CR/CRN MULTILAYER COATINGS; COATED STAINLESS-STEEL; CHROMIUM NITRIDE; HARD COATINGS; TRIBOLOGICAL PROPERTIES; BILAYER PERIOD; BEHAVIOR; GROWTH; WEAR;
D O I：
10.1016/j.surfcoat.2016.04.069
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
This paper presents the corrosion resistance of CrN monolayer coatings and CrCN/CrN multilayer coatings deposited by cathodic arc evaporation onto X39Cr13 stainless steel. Corrosion tests of the coating-substrate systems were conducted in Ringer's and Hank's solutions, usually used as infusion liquids. The parameters such as corrosion potential, corrosion current density and polarisation resistance were determined on the basis of the potentiodynamic polarisation curves. The corrosion properties of coatings in as-deposited state and after the polishing were compared. The results show that coated substrates are characterised by under half the corrosion potential and 10-times lower corrosion current density compared to the reference substrate (without coating). The corrosion parameters for polished coatings are slightly worse than unpolished, which is related to the method of coating deposition. The amount and distribution of macroparticles on the surface of the tested coatings are also presented. (C) 2016 Elsevier B.V. All rights reserved.
引用
收藏
页码：7 / 14
页数：8
相关论文
共 50 条
  • [31] Comparison of the wear and corrosion behavior between CrN and AlCrN coatings deposited by Arc-PVD method
    Jokar, Katayoon
    Elmkhah, Hassan
    Fattah-alhosseini, Arash
    Babaei, Kazem
    Zolriasatein, Ashkan
    MATERIALS RESEARCH EXPRESS, 2019, 6 (11)
  • [32] Structure and Properties of AlCrN Coatings Deposited Using Cathodic Arc Evaporation
    Warcholinski, Bogdan
    Gilewicz, Adam
    Myslinski, Piotr
    Dobruchowska, Ewa
    Murzynski, Dawid
    COATINGS, 2020, 10 (08)
  • [33] The role of the growth defects on the corrosion resistance of CrN/NbN superlattice coatings deposited at low temperatures
    Lewis, DB
    Creasey, SJ
    Wüstefeld, C
    Ehiasarian, AP
    Hovsepian, PE
    THIN SOLID FILMS, 2006, 503 (1-2) : 143 - 148
  • [34] Structure and Corrosion Resistance of Vacuum-Arc Multi-period CrN/Cu Coatings
    Postelnyk, Hanna
    Sobol, Oleg
    Chocholaty, Ondrej
    Knyazev, Sergey
    ADVANCES IN DESIGN, SIMULATION AND MANUFACTURING III: MANUFACTURING AND MATERIALS ENGINEERING, VOL 1, 2020, : 532 - 541
  • [35] Corrosion resistance and antifouling activities of silver-doped CrN coatings deposited by magnetron sputtering
    Cai, Qun
    Li, Shuxin
    Pu, Jibin
    Bai, Xuebing
    Wang, Haixin
    Cai, Zhaobing
    Wang, Xuezhen
    SURFACE & COATINGS TECHNOLOGY, 2018, 354 : 194 - 202
  • [36] Oxygen effect on the mechanical behaviors of Cr(N,O)/CrN double-layered coatings by cathodic arc evaporation
    Ho, WY
    Hsu, CH
    Huang, DH
    Cheng, YP
    Lin, YC
    Chang, CL
    SURFACE & COATINGS TECHNOLOGY, 2004, 188 : 129 - 134
  • [37] Spectroscopic investigations of Cr, CrN and TiCr anti-multipactor coatings grown by cathodic-arc reactive evaporation
    Fuentes, G. G.
    Rodriguez, R. J.
    Garcia, M.
    Montero, I.
    de Segovia, J. L.
    APPLIED SURFACE SCIENCE, 2007, 253 (18) : 7627 - 7631
  • [38] Erosion and corrosion behaviors of ADI deposited TiN/TiAIN coatings by cathodic arc evaporation
    Hsu, CH
    Lu, JK
    Lai, KL
    Chen, ML
    MATERIALS TRANSACTIONS, 2005, 46 (06) : 1417 - 1424
  • [39] Tuning bilayer period of AlN/CrN superlattice coatings deposited using cathodic arc technique for superior mechanical properties and thermal stability
    Mundotia, R.
    Ghorude, T.
    Kothari, D. C.
    Kale, A.
    Thorat, N.
    APPLIED SURFACE SCIENCE ADVANCES, 2022, 7
  • [40] Effect of periodicity on hardness and scratch resistance of CrN/NbN nanoscale multilayer coating deposited by cathodic arc technique
    Araujo, Juliano Avelar
    Araujo, Gisela Marques
    Souza, Roberto Martins
    Tschiptschin, Andre Paulo
    WEAR, 2015, 330 : 469 - 477
12345