Buckling and spalling failure of alumina grown by oxidation on ODS FeCrAl alloys

被引：3
|
作者：
Sniezewski, Julien [1 ]
Lours, Philippe [1 ]
Le Maoult, Yannick [1 ]
机构：
[1] Univ Toulouse, Inst Clement Ader, F-81013 Albi, France
来源：
MATERIALS AT HIGH TEMPERATURES | 2011年 / 28卷 / 01期
关键词：
in situ analysis; oxidation; buckling; spallation; SPALLATION; PM2000;
D O I：
10.3184/096034011X12962385894289
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In situ investigation of thermal shocks imposed to alumina grown on FeCrAl alloy at high temperature shows that interfacial buckling is the preferential route to spallation. Various parameters, either intrinsic or extrinsic to the substrate/oxide system, are analysed in terms of variation in interfacial fracture energies and propensity of alloy grains to wrinkle during high temperature exposure depending On their crystal orientation.
引用
收藏
页码：17 / 20
页数：4
相关论文
共 50 条
  • [31] Recent Progress on Creep Properties of ODS FeCrAl Alloys for Advanced Reactors
    Jia, Haodong
    Wang, Yingjie
    Wang, You
    Han, Lu
    Zhang, Yujuan
    Zhou, Zhangjian
    MATERIALS, 2023, 16 (09)
  • [32] Development and characterization of γ/α transformable FeCrAl-ODS alloys by cobalt addition
    Zhang, S. H.
    Ukai, S.
    Nishikawa, T.
    Aghamiri, S. M. S.
    Oono, N.
    Hayashi, S.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 797 : 390 - 398
  • [33] Development of nano-oxide particles dispersed alumina scale formed on Zr-added FeCrAl ODS ferritic alloys
    Yu, Hao
    Kondo, Sosuke
    Kasada, Ryuta
    Oono, Naoko
    Hayashi, Shigenari
    Ukai, Shigeharu
    NUCLEAR MATERIALS AND ENERGY, 2020, 25
  • [34] Microstructural development of α alumina scales developed on FeCrAl alloys
    Prior, D. J.
    Al-Badairy, H.
    Seward, G. G. E.
    Veltkamp, C. J.
    Tatlock, G. J.
    MATERIALS SCIENCE AND TECHNOLOGY, 2006, 22 (11) : 1316 - 1324
  • [35] Effects of zirconium and oxygen on the oxidation of FeCrAl-ODS alloys under air and steam conditions up to 1500 °C
    Maeda, T.
    Ukai, S.
    Hayashi, S.
    Oono, N.
    Shizukawa, Y.
    Sakamoto, K.
    JOURNAL OF NUCLEAR MATERIALS, 2019, 516 : 317 - 326
  • [36] Aluminium depletion in FeCrAl alloys during oxidation
    Lesage, B
    Maréchal, L
    Huntz, AM
    Molins, R
    DIFFUSIONS IN MATERIALS: DIMAT2000, PTS 1 & 2, 2001, 194-1 : 1707 - 1712
  • [37] The oxidation lifetime of commercial FeCrAl(RE) alloys
    Newton, R
    Bennett, MJ
    Wilber, JP
    Nicholls, JR
    Naumenko, D
    Quadakkers, WJ
    Al-Badairy, H
    Tatlock, G
    Strehl, G
    Borchardt, G
    Kolb-Telieps, A
    Jönsson, B
    Westerlund, A
    Guttmann, V
    Maier, M
    Beaven, P
    LIFETIME MODELLING OF HIGH TEMPERATURE CORROSION PROCESSES, 2001, (34): : 15 - 36
  • [38] The effect of thermal cycling on the mechanical failure of alumina scales formed on commercial FeCrAl-RE alloys
    Wilber, JP
    Bennett, MJ
    Nicholls, JR
    CYCLIC OXIDATION OF HIGH TEMPERATURE MATERIALS: MECHANISMS, TESTING METHODS, CHARACTERISATION AND LIFE TIME ESTIMATION, 1999, (27): : 133 - 147
  • [39] Effect of explosive compaction on microstructure of ODS FeCrAl alloy fabricated by oxidation method
    Yan, Fuzhao
    Li, Jing
    Xiong, Liangyin
    Liu, Shi
    MATERIALS RESEARCH EXPRESS, 2021, 8 (04)
  • [40] On the influence of yttrium and sulphur on the high temperature oxidation behaviour of alumina-forming high purity FeCrAl alloys
    Glazkov, A
    Gobel, M
    Jedlinski, J
    Schimmelpfennig, J
    Borchardt, G
    Weber, S
    Scherrer, S
    LeCoze, J
    JOURNAL DE PHYSIQUE IV, 1995, 5 (C7): : 381 - 385
12345