Electrochemical corrosion behavior of electroless Ni-P coating in NaCl and H2SO4 solutions

被引：28
|
作者：
Wang, L. L. [2 ]
Chen, H. J. [2 ]
Hao, L. [1 ]
Lin, A. [1 ]
Gan, F. X. [1 ,3 ]
机构：
[1] Wuhan Univ, Dept Environm Engn, Sch Resource & Environm Sci, Wuhan 430079, Peoples R China
[2] Xinyang Normal Univ, Coll Chem & Chem Engn, Xinyang 464000, Peoples R China
[3] Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China
来源：
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION | 2011年 / 62卷 / 11期
关键词：
corrosion behavior; EIS; electrochemical test; electroless Ni-P coating; H [!sub]2[!/sub]SO[!sub]4[!/sub; NaCl;
D O I：
10.1002/maco.200905575
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Electrochemical corrosion behavior of electroless Ni-P coating in NaCl and H2SO4 solutions were studied by potentiodynamic polarization curves and electrochemical impedance spectra techniques, as well as the corrosion morphology was characterized. The results indicate that electroless Ni-P coating with about 25 mu m is stable in 30 days immersion in NaCl solution. Although it was corroded with prolonged immersion days, the corrosive medium has not penetrated through the coating. During the H2SO4 concentration ranging from 5 to 10%, the corrosion current density of electroless Ni-P coating increased due to the intensified anodic dissolution process; in 15% H2SO4 solution, electroless Ni-P coating shows obvious anodic passivation effect.
引用
收藏
页码：1003 / 1007
页数：5
相关论文
共 50 条
  • [31] STUDY OF THE FRICTION AND WEAR BEHAVIOR OF ELECTROLESS NI-P COATING
    YU, LG
    ZHANG, XS
    THIN SOLID FILMS, 1993, 229 (01) : 76 - 82
  • [32] The Electrochemical Behavior of Ni-base Metallic Glasses Containing Cr in H2SO4 Solutions
    Arab, Sanaa. T.
    Emran, Khadijah. M.
    Al-Turaif, Hamad A.
    JOURNAL OF THE KOREAN CHEMICAL SOCIETY-DAEHAN HWAHAK HOE JEE, 2012, 56 (04): : 448 - 458
  • [33] Evaluation of the corrosion resistance of electroless Ni-P and Ni-P composite coatings by electrochemical impedance spectroscopy
    J. Balaraju
    T. Sankara Narayanan
    S. Seshadri
    Journal of Solid State Electrochemistry, 2001, 5 : 334 - 338
  • [34] Evaluation of the corrosion resistance of electroless Ni-P and Ni-P composite coatings by electrochemical impedance spectroscopy
    Balaraju, JN
    Narayanan, TSNS
    Seshadri, SK
    JOURNAL OF SOLID STATE ELECTROCHEMISTRY, 2001, 5 (05) : 334 - 338
  • [35] Corrosion characteristics of electroless Ni-P coating in dichloropropanol (DCP) solution
    Wu, Y. H.
    Liu, T. M.
    Luo, S. X.
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2011, 46 (03) : 245 - 248
  • [36] Erosion-Corrosion Behavior and Mechanism of Heated Electroless Ni-P Coating under Flow
    Tang, Yi-Rong
    Wang, Qin-Ying
    Guo, Hai-Chang
    Xi, Yu-Chen
    Dong, Li-Jin
    Wang, Xian-Zong
    MATERIALS TRANSACTIONS, 2020, 61 (11) : 2162 - 2169
  • [37] DISSOLUTION OF GLASSY Ni-P ALLOYS IN H2SO4 AND HCl ELECTROLYTES.
    Diegle, R.B.
    Sorensen, N.R.
    Nelson, G.C.
    1769, (133):
  • [38] Corrosion behavior of electroless Ni-P/TiO2 nanocomposite coatings
    Shoeib, Madiha A.
    Kamel, Medhat M.
    Rashwan, Salah M.
    Hafez, Omar M.
    SURFACE AND INTERFACE ANALYSIS, 2015, 47 (06) : 672 - 680
  • [39] Corrosion behavior of alumina ceramics in aqueous HCl and H2SO4 solutions
    Curkovic, Lidija
    Jelaca, Mirjana Fuduric
    Kurajica, Stanislav
    CORROSION SCIENCE, 2008, 50 (03) : 872 - 878
  • [40] A Comprehensive Investigation into the Corrosion Mechanism of an Electroless Ni-P Coating in CO2-Saturated NaCl Solution: Degradation or Penetration?
    Huang, Chenhao
    Yan, Jing
    Fan, Hongyuan
    Sun, Lan
    Wang, Jun
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2024, 55 (10): : 4249 - 4268
12345