Lattice disorder and radiation enhanced annealing in La-implanted TiO2 single crystals

被引:22
|
作者
Fromknecht, R
Meyer, O
机构
[1] Forschungszentrum Karlsruhe, Technik und Umwelt, Inst. fur Nukleare Festkorperphysik, D-76021 Karlsruhe
关键词
lattice disorder; radiation enhanced annealing; La ions; TiO2 single crystals;
D O I
10.1016/0254-0584(96)80047-2
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Rutherford backscattering spectrometry and channeling were used to characterize the disorder produced by implantation of La ions into TiO2 (rutile) single crystals at substrate temperatures T-i between 77 and 1100 K. Complete amorphization was observed at T-i of 77 and 300 K for La fluences of 1 x 10(15) cm(-2) and 2 x 10(15) cm(-2), respectively. At T-i equal to 300 K acid fluences of 1 x 10(15) cm(-2), radiation-enhanced annealing starts to affect the disorder profile. The recovery occurs preferentially in the near-surface region. With increasing T-i, two recovery stages of the lattice disorder, between 300 and 500 EC and above 700 K, have been observed. These stages are about 200 K lower than those observed for subsequent isochronal annealing of an amorphous TiO2 layer. At T-i equal to 1100 K recovery of the lattice disorder was nearly complete. A minimum yield of 2.5% was reached, similar to that of the virgin crystal. Radiation-enhanced diffusion of La into TiO2 leads to an estimated substitutional component of 35%.
引用
收藏
页码:50 / 54
页数:5
相关论文
共 50 条
  • [22] Mesoporous TiO2 single crystals delivering enhanced mobility and optoelectronic device performance
    Crossland, Edward J. W.
    Noel, Nakita
    Sivaram, Varun
    Leijtens, Tomas
    Alexander-Webber, Jack A.
    Snaith, Henry J.
    NATURE, 2013, 495 (7440) : 215 - 219
  • [23] Rutile TiO2 single crystals delivering enhanced photocatalytic oxygen evolution performance
    Fu, Bing
    Wu, Zhijiao
    Guo, Kai
    Piao, Lingyu
    NANOSCALE, 2021, 13 (18) : 8591 - 8599
  • [24] Enhanced Capacitance of TiO2 Single Crystals Through Chemically Deposited Graphene Films
    Liang, Y. Q.
    Gao, Z. H.
    Cui, Z. D.
    Zhu, S. L.
    Li, Z. Y.
    Yang, X. J.
    JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2015, 15 (06) : 4567 - 4573
  • [25] Mesoporous TiO2 single crystals delivering enhanced mobility and optoelectronic device performance
    Edward J. W. Crossland
    Nakita Noel
    Varun Sivaram
    Tomas Leijtens
    Jack A. Alexander-Webber
    Henry J. Snaith
    Nature, 2013, 495 : 215 - 219
  • [26] Enhanced photocatalytic activity of porous single crystal TiO2/CNT composites by annealing process
    Park, Chae Hee
    Lee, Chang Min
    Choi, Jong Won
    Park, Geun Chul
    Joo, Jinho
    CERAMICS INTERNATIONAL, 2018, 44 (02) : 1641 - 1645
  • [27] Magnetism of a Nitrogen-Implanted TiO2 Single Crystal
    Liu Chun-Ming
    Xiang Xia
    Zhang Yan
    Jiang Yong
    Zu Xiao-Tao
    CHINESE PHYSICS LETTERS, 2011, 28 (12)
  • [28] Formation of polycrystalline TiO2 on the ablated surfaces of RbTiOPO4 single crystals by thermal annealing
    Carvajal, J. J.
    Kumar, G. Raj
    Massons, J.
    Vazquez de Aldana, J. R.
    Gallardo, I.
    Moreno, P.
    Roso, L.
    Diaz, F.
    Aguilo, M.
    CRYSTENGCOMM, 2014, 16 (20): : 4281 - 4288
  • [29] OBSERVATION OF ETCH PATTERNS IN TIO2 SINGLE CRYSTALS
    NAKAZUMI, Y
    SUZUKI, K
    YAZIMA, T
    JOURNAL OF THE PHYSICAL SOCIETY OF JAPAN, 1962, 17 (11) : 1806 - &
  • [30] Hydrogen:: A metastable donor in TiO2 single crystals
    Chen, W. P.
    Wang, Y.
    Chan, H. L. W.
    APPLIED PHYSICS LETTERS, 2008, 92 (11)