Rare earth ion size effects and enhanced critical current densities in Y2/3Sm1/3Ba2Cu3O7-x coated conductors -: art. no. 032505

被引：65
|
作者：
MacManus-Driscoll, JL [1 ]
Foltyn, SR
Maiorov, B
Jia, QX
Wang, H
Serquis, A
Civale, L
Lin, Y
Hawley, ME
Maley, MP
Peterson, DE
机构：
[1] Los Alamos Natl Lab, Superconductiv Technol Ctr, Los Alamos, NM 87545 USA
[2] Univ Cambridge, Dept Mat Sci & Met, Cambridge CB2 3QZ, England
来源：
APPLIED PHYSICS LETTERS | 2005年 / 86卷 / 03期
关键词：
D O I：
10.1063/1.1851006
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
The influence of rare earth (RE) ion size on critical current density (J(c)) in epitaxial films of superconducting REBa2CuO7-x was studied, where RE is the mixture of two or three rare earth ions. No systematic dependence of Jc on RE ion size was found. However, strongly enhanced critical current densities (J(c)'s) were found for the composition Y2/3SM1/3Ba2Cu3O7-x (YSmBCO). In similar to1-mum-thick films, J(c)'s as high as 4.7X 10(6) A cm(-2) (7.5.5 K, 0 T) and 1 X 10(4) A cm(-2) (75.5 K, 5 T) were obtained on single crystals and 6 X 104 A cm(-2) (75.5 K, 5 T) on buffered metal. The values are up to a factor of 3 higher than for comparative YBCO samples. (C) 2005 American Institute of Physics.
引用
收藏
页码：1 / 3
页数：3
相关论文
共 50 条
  • [31] Structural and magnetotransport properties of YBa2Cu3O7-δ/Y2O3 quasimultilayers -: art. no. 123906
    Cai, C
    Hänisch, J
    Hühne, R
    Stehr, V
    Mickel, C
    Gemming, T
    Holzapfel, B
    JOURNAL OF APPLIED PHYSICS, 2005, 98 (12)
  • [32] Low-field transport relaxation measurements in superconducting Y1Ba2Cu3O7-δ -: art. no. 144513
    Kiliç, K
    Kiliç, A
    Yetis, H
    Çetin, O
    PHYSICAL REVIEW B, 2003, 68 (14):
  • [33] RARE-EARTH(RE)-BARIUM SOLUBILITY BEHAVIOUR IN Ba2 - //xRE//x)Cu3O7 + delta AND Sm(Ba2 minus //xRE//x)Cu 3O7 + delta
    Suzuki, Atsushi
    Sampathkumarasn, E.V.
    Kohn, Kay
    Shibuya, Takashi
    Tohdake, Ayako
    Ishikawa, Masayasu
    Japanese Journal of Applied Physics, Part 2: Letters, 1988, 27 (05): : 792 - 794
  • [34] Strongly coupled critical current density values achieved in Y1Ba2Cu3O7-δ coated conductors with near-single-crystal texture
    Foltyn, SR
    Arendt, PN
    Jia, QX
    Wang, H
    MacManus-Driscoll, JL
    Kreiskott, S
    DePaula, RF
    Stan, L
    Groves, JR
    Dowden, PC
    APPLIED PHYSICS LETTERS, 2003, 82 (25) : 4519 - 4521
  • [35] Effects of epitaxial strain on the growth mechanism in YBa2Cu3O7-x thin films in YBa2Cu3O7-x/PrBa2Cu3O7 superlattices -: art. no. 174514
    Varela, M
    Grogger, W
    Arias, D
    Sefrioui, Z
    León, C
    Vazquez, L
    Ballesteros, C
    Krishnan, KM
    Santamaría, J
    PHYSICAL REVIEW B, 2002, 66 (17): : 1 - 6
  • [36] MAGNETIC HYSTERESIS AND CRITICAL CURRENT DENSITIES OF POLYCRYSTALLINE REBA2CU3O7-Y
    XU, Y
    GUAN, W
    ZEIBIG, K
    HEIDEN, C
    CRYOGENICS, 1989, 29 (3A) : 281 - 285
  • [37] CRITICAL CURRENT DENSITIES OF MELT-TEXTURED YBA2CU3O7-Y
    FAN, HC
    ZHANG, YT
    JIN, X
    LU, M
    JI, HL
    XU, XN
    YAO, XX
    REN, HT
    XIAO, L
    HE, Q
    PHYSICA C, 1991, 185 : 2331 - 2332
  • [38] PULSED LASER DEPOSITION OF THIN SUPERCONDUCTING FILMS OF HO1BA2CU3O7-X AND Y1BA2CU3O7-X
    GEOHEGAN, DB
    MASHBURN, DN
    CULBERTSON, RJ
    PENNYCOOK, SJ
    BUDAI, JD
    VALIGA, RE
    SALES, BC
    LOWNDES, DH
    BOATNER, LA
    SONDER, E
    ERES, D
    CHRISTEN, DK
    CHRISTIE, WH
    JOURNAL OF MATERIALS RESEARCH, 1988, 3 (06) : 1169 - 1179
  • [39] High critical current densities in YBa2Cu3O7-x films grown at high rates by hybrid liquid phase epitaxy -: art. no. 252507
    Kursumovic, A
    Evetts, JE
    MacManus-Driscoll, JL
    Maiorov, B
    Civale, L
    Wang, H
    Jia, QX
    Foltyn, SR
    APPLIED PHYSICS LETTERS, 2005, 87 (25) : 1 - 3
  • [40] Critical current degradation in an epoxy-impregnated rare-earth Ba2Cu3O7-x coated conductor caused by damage during a quench
    Liu, Donghui
    Yong, Huadong
    Zhou, Youhe
    APPLIED MATHEMATICS AND MECHANICS-ENGLISH EDITION, 2024, 45 (09) : 1557 - 1572
12345