Austempering of spheroidal graphite cast iron

被引：10
|
作者：
El-Baradie, ZM [1 ]
Ibrahim, MM [1 ]
El-Sisy, IA [1 ]
Abd El-Hakeem, AA [1 ]
机构：
[1] Cairo Univ, Fac Engn, Cairo, Egypt
来源：
MATERIALS SCIENCE | 2004年 / 40卷 / 04期
关键词：
D O I：
10.1007/s11003-005-0071-4
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
We study gray spherulitic cast iron, its microstructure, hardness ultimate strength in tension, elongation, and impact toughness as functions of the duration of isothermal austenitizing in the bainite region at 350 and 400 degrees C after austenitizing at 900 degrees C. As the temperature of quenching increases from 350 to 400 degrees C, the microstructure of the analyzed cast iron changes from lower to higher bainite and the amount of retained austenite increases (its maximum is attained after 1 h). At the same time, the ultimate strength in tension and hardness decrease, whereas the elongation and fracture toughness increase.
引用
收藏
页码：523 / 528
页数：6
相关论文
共 50 条
  • [31] Special Features of the Microstructure of Cast Iron with Spheroidal Graphite
    A. S. Chaus
    Metal Science and Heat Treatment, 2015, 57 : 419 - 427
  • [32] Damage kinetics in ferritic spheroidal graphite cast iron
    Guillemer-Neel, C
    Feaugas, X
    Bobet, V
    Clavel, M
    ECF 12: FRACTURE FROM DEFECTS, VOLS. I-III, 1998, : 721 - 726
  • [33] OBSERVATION OF SPHEROIDAL GRAPHITE IN DUCTILE CAST IRON BY TEM
    Hara, T.
    Maekawa, T.
    Kawabata, T.
    Terayama, K.
    Ikeno, S.
    Matsuda, K.
    ARCHIVES OF METALLURGY AND MATERIALS, 2013, 58 (02) : 431 - 432
  • [34] Fatigue damage in Spheroidal Graphite cast Iron (SGI)
    Nadot, Y
    Mendez, J
    Ranganathan, N
    Beranger, AS
    ECF 11 - MECHANISMS AND MECHANICS OF DAMAGE AND FAILURE, VOLS I-III, 1996, : 1155 - 1160
  • [35] Wear Behavior and Mechanism of Spheroidal Graphite Cast Iron
    Yang Zi-run
    Li Dong-sheng
    Wang Lan
    Wang Shu-qi
    Wei Min-xian
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2013, 20 (10) : 81 - 86
  • [36] SPECIAL FEATURES OF THE MICROSTRUCTURE OF CAST IRON WITH SPHEROIDAL GRAPHITE
    Chaus, A. S.
    METAL SCIENCE AND HEAT TREATMENT, 2015, 57 (7-8) : 419 - 427
  • [37] Improvement of magnetic characteristic in spheroidal graphite cast iron
    Matsumoto, Akikazu
    Kanetake, Naoyuki
    PRICM 6: SIXTH PACIFIC RIM INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS AND PROCESSING, PTS 1-3, 2007, 561-565 : 1123 - 1126
  • [38] Progress of erosive wear in spheroidal graphite cast iron
    Shimizu, K
    Noguchi, T
    Kamada, T
    Takasaki, H
    WEAR, 1996, 198 (1-2) : 150 - 155
  • [39] ISOTHERMAL AUSTENITIZING OF SPHEROIDAL GRAPHITE CAST-IRON
    WADE, N
    UEDA, Y
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1980, 20 (12) : 849 - 856
  • [40] MECHANISM OF CRYSTALLIZATION OF SPHEROIDAL GRAPHITE IN CAST-IRON
    SYTNIK, NM
    METAL SCIENCE AND HEAT TREATMENT, 1991, 33 (3-4) : 317 - 322
12345