Synthesis and characterization of Sb-doped SnO2-(CeO2-TiO2) composite thin films deposited on glass substrates for antistatic electricity and UV-shielding

被引：23

作者：

Wu Shuo ^{[1
]}

Zhao Qingnan ^{[1
]}

Miao Dengkui ^{[1
]}

Dong Yuhong ^{[2
]}

机构：

[1] Wuhan Univ Technol, Minist Educ, Key Lab Silicate Mat Sci & Engn, Wuhan 430070, Peoples R China

[2] Jiangsu Xiuqiang Glasswork CO Ltd, Suqian 223800, Peoples R China

来源：

JOURNAL OF RARE EARTHS | 2010年 / 28卷

关键词：

antistatic electricity; UV shielding; ATO-(CeO2-TiO2) thin films; hydrothermal process; rare earths; TRANSPARENT CONDUCTING OXIDE; SOL-GEL; COATINGS;

D O I：

10.1016/S1002-0721(10)60377-8

中图分类号：

O69 [应用化学];

学科分类号：

081704 ;

摘要：

Sb-doped SnO2 (ATO)-(CeO2-TiO2) thin Films were deposited on glass substrates using the mixed solution including CeO2-TiO2 precursor and ATO particles by sol-gel dip coating process. ATO particles were prepared using low-temperature hydrothermal process. The mixed molar ratio of ATO to (CeO2-TiO2) vs the properties of CeO2-TiO2 thin film was investigated. The optical properties of the films were characterized by UV-visible transmission and infrared reflection spectra, the sheet resistance of ATO particles and films were measured by rubber sheeter (MYI-50) and four-point probe (HisuperGroup Inc, SDY-5), the surface morphology and structure of the films were analyzed using 3D Digitale Mikroskop and X-ray diffraction (XRD), respectively. The results showed that the ATO precursor solution lost weight completely at about 500 degrees C, and the ATO particles was obtained, which indicated the same rutile lattice structure as SnO2. The glass substrates coated with ATO-(CeO2-TiO2) thin films showed better properties in antistatic electricity (10(4)-10(6) Omega/square), shielding UV (almost 100%), visible light transmission (70%) and infrared reflection (>30%).

引用

页码：189 / 193

页数：5

共 50 条

[31] Comparison of some physical properties for SnO2, SnO2: F and SnO2: Sb films deposited on glass substrates
Tatar, Demet
Turgut, Guven
Sonmez, Erdal
Duzgun, Bahattin
JOURNAL OF OPTOELECTRONICS AND ADVANCED MATERIALS, 2013, 15 (9-10): : 1026 - 1031
[32] Limits of carrier mobility in Sb-doped SnO2 conducting films deposited by reactive sputtering
Bissig, B.
Jaeger, T.
Ding, L.
Tiwari, A. N.
Romanyuk, Y. E.
APL MATERIALS, 2015, 3 (06):
[33] The morphology of CdS thin films deposited on SnO2-coated glass substrates
Hasoon, FS
Al-Jassim, MM
Swartzlander, A
Sheldon, P
Al-Douri, AAJ
Alnajjar, AA
CONFERENCE RECORD OF THE TWENTY SIXTH IEEE PHOTOVOLTAIC SPECIALISTS CONFERENCE - 1997, 1997, : 543 - 546
[34] Sb:SnO2 Thin Films- Synthesis and Characterization
Bhadrapriya, B. C.
Varghese, Anitta Rose
Amarendra, G.
Hussain, Shamima
9TH NATIONAL CONFERENCE ON THERMOPHYSICAL PROPERTIES (NCTP-2017), 2018, 1951
[35] Synthesis and Photoactivity of SnO2-Doped TiO2 Thin Films
Jung, Miewon
Kwak, Yunjung
JOURNAL OF THE KOREAN CERAMIC SOCIETY, 2007, 44 (11) : 650 - 654
[36] UV-shielding efficiency of TiO2-polystyrene thin films prepared by solution cast method
Acharya, Aman Deep
Sarwan, Bhawna
Sharma, R.
Moghe, S.
Shrivastava, S. B.
Ganesan, V.
FRONTIERS OF PHYSICS AND PLASMA SCIENCE, 2017, 836
[37] Crystal structure and photocatalytic characteristics of nanoscale Sb-doped TiO2 thin films
Ren, Da-sen
Zhang, Zhuang-jian
CHINESE JOURNAL OF CHEMICAL PHYSICS, 2006, 19 (06) : 549 - 554
[38] Sol-gel synthesis, characterization and optical properties of mercury-doped TiO2 thin films deposited on ITO glass substrates
Mechiakh, R.
Ben Sedrine, N.
Chtourou, R.
APPLIED SURFACE SCIENCE, 2011, 257 (21) : 9103 - 9109
[39] Influence of Chemisorption of Various Gases on the Electrical Conductivity of Sb-DOPED SnO2 Thin Films
Szklarski, Zbigniew
Rekas, Mieczyslaw
Studies in Surface Science and Catalysis, 1985, 23 (0C) : 219 - 220
[40] TiO2 thin films doped by Ce, Nb, Fe, deposited onto ITO/glass substrates
Mardare, D.
Apostol, E.
JOURNAL OF OPTOELECTRONICS AND ADVANCED MATERIALS, 2006, 8 (03): : 914 - 916

← 1 2 3 4 5 →