Thermal conductivity of zirconia-alumina composites

Ten mole percent of yttria-stabilized zirconia (10YSZ)-alumina composites containing 0-30 mol% alumina were fabricated by hot pressing at 1500 degrees C in vacuum. Thermal conductivity of the composites, determined at various temperatures using a steady-state laser heat flux technique, increased with increase in alumina content. Composites containing 0, 5, and 10 mol% alumina did not show any change in thermal conductivity with temperature. However, those containing 20 and 30 mol% alumina showed a decrease in thermal conductivity with increase in temperature. The measured values of thermal conductivity were in good agreement with those calculated from the Maxwell-Eucken model where one phase is uniformly dispersed within a second major continuous phase. Published by Elsevier Ltd and Techna Group S.r.l.