A comparative study of Pt/C and Pt-MoOx/C catalysts with various compositions for methanol electro-oxidation

被引：65
|
作者：
Ma, Liang [1 ,2 ]
Zhao, Xiao [1 ,2 ]
Si, Fengzhan [1 ,2 ]
Liu, Changpeng [1 ]
Liao, Jianhui [1 ]
Liang, Liang [1 ]
Xing, Wei [1 ]
机构：
[1] Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Electroanalyt Chem, Changchun 130022, Peoples R China
[2] Chinese Acad Sci, Grad Univ, Beijing 100049, Peoples R China
来源：
ELECTROCHIMICA ACTA | 2010年 / 55卷 / 28期
基金：
中国国家自然科学基金;
关键词：
Pt-MoOx/C; Methanol electro oxidation; Mass activity; Specific activity; Electrocatalyst; Metal-support interaction; CARBON-SUPPORTED PLATINUM; ENHANCED CO-TOLERANCE; MEMBRANE FUEL-CELLS; ANODE CATALYST; FORMIC-ACID; RU ELECTROCATALYST; H-2/CO MIXTURES; OXIDATION; ALLOY; NANOPARTICLES;
D O I：
10.1016/j.electacta.2010.08.034
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
The methanol electro-oxidation behaviors on the Pt-MoOx/C catalysts with various compositions were investigated and compared to those of Pt/C catalyst by cyclic voltammetry and chronoamperometry The Pt-MoOx/C catalysts were prepared by depositing Pt on the MoOx/C support obtained by precipitation-reduction method in advance The physical properties of the prepared catalysts were characterized by XRD XPS EDX and TEM From the results of XRD and TEM it was shown that the MoOx/C support facilitated the dispersion of Pt particles All the Pt-MoOx/C catalysts showed relative lower Mo contents comparing to their nominal values No PtMo alloy was formed in these catalysts which were affirmed by XPS and XRD It was found that all the Pt-MoOx/C catalysts showed higher mass activity (normalized to the mass of Pt) but lower specific activity (normalized to the electrochemical active surface areas) for methanol oxidation than the Pt/C catalyst With the increase of Mo contents in Pt-MoOx/C catalysts the activities of Pt-MoOx/C catalysts decreased Combined with the composition and structure analyses the differences in methanol oxidation on these catalysts were attributed to the interaction between the Pt particles and the MoOx/C support It was suggested that the Pt metal-MoOx/C support interaction resulted in two effects One was decreasing the Pt particle size the other was decreasing the specific activities of these catalysts for methanol oxidation Comprising these two contradictory effects the mass activities of these catalysts for methanol oxidation increased (C) 2010 Elsevier Ltd All rights reserved
引用
收藏
页码：9105 / 9112
页数：8
相关论文
共 50 条
  • [21] Pt catalysts on PANI coated WC/C nanocomposites for methanol electro-oxidation and oxygen electro-reduction in DMFC
    Yaldagard, Maryam
    Jahanshahi, Mohsen
    Seghatoleslami, Naser
    APPLIED SURFACE SCIENCE, 2014, 317 : 496 - 504
  • [22] Preparation of Pt/mesoporous carbon catalysts and their application to the methanol electro-oxidation
    Kim, Heesoo
    Kim, Pil
    Choi, Kyunghee
    Yi, Jongheop
    NEW DEVELOPMENT AND APPLICATION IN CHEMICAL REACTION ENGINEERING, 4TH ASIA-PACIFIC CHEMICAL REACTION ENGINEERING SYMPOSIUM (APCRE 05), 2006, 159 : 609 - 612
  • [23] Electro-oxidation of ethanol on ternary Pt-Sn-Ce/C catalysts
    Jacob, Juliana M.
    Corradini, Patricia G.
    Antolini, Ermete
    Santos, Nathalia Abe
    Perez, Joelma
    APPLIED CATALYSIS B-ENVIRONMENTAL, 2015, 165 : 176 - 184
  • [24] Investigation of Pt/WC/C catalyst for methanol electro-oxidation and oxygen electro-reduction
    Jeon, Min Ku
    Lee, Ki Rak
    Lee, Won Su
    Daimon, Hideo
    Nakahara, Akemi
    Woo, Seong Ihl
    JOURNAL OF POWER SOURCES, 2008, 185 (02) : 927 - 931
  • [25] A proper amount of carbon nanotubes for improving the performance of Pt-Ru/C catalysts for methanol electro-oxidation
    Chi, Ching-Fa
    Yang, Ming-Chang
    Weng, Hung-Shan
    JOURNAL OF POWER SOURCES, 2009, 193 (02) : 462 - 469
  • [26] Glycerol and Methanol Electro-oxidation at Pt/C-ITO under Alkaline Condition
    Ottoni, Cristiane Angelica
    Domingues Ramos, Carlos Eduardo
    da Silva, Sirlane Gomes
    Spinace, Estevan Vitorio
    Brambilla de Souza, Rodrigo Fernando
    Oliveira Neto, Almir
    ELECTROANALYSIS, 2016, 28 (10) : 2552 - 2558
  • [27] Electrochemical impedance studies of methanol electro-oxidation on Pt/C thin film electrode
    Hsing, IM
    Wang, X
    Leng, YJ
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2002, 149 (05) : A615 - A621
  • [28] A novel catalyst Pt@NiPcTs/C: Synthesis, structural and electro-oxidation for methanol
    Kang, Jianqiang
    Ma, Wentao
    Wu, Jingjie
    Pan, Mu
    CATALYSIS COMMUNICATIONS, 2009, 10 (08) : 1271 - 1274
  • [29] Carbon xerogel supported Pt and Pt-Ni catalysts for electro-oxidation of methanol in basic medium
    Samant, PV
    Fernandes, JB
    Rangel, CM
    Figueiredo, JL
    CATALYSIS TODAY, 2005, 102 : 173 - 176
  • [30] Investigation of Pt–Ru nanoparticle catalysts for low temperature methanol electro-oxidation
    G. Garcia
    V. Baglio
    A. Stassi
    E. Pastor
    V. Antonucci
    A. S. Aricò
    Journal of Solid State Electrochemistry, 2007, 11 : 1229 - 1238
12345