Distribution of the precipitates on the grain boundaries in Fe-3%Si steel during secondary recrystallization annealing

被引：1
|
作者：
Yim, Jung-Ryoul [1 ]
Min, Ah-Ri [1 ]
Park, Jong-Tae [2 ]
Joo, Young-Chang [1 ]
机构：
[1] Seoul Natl Univ, Sch Mat Sci & Engn, Seoul, South Korea
[2] POSCO, Tech Res Lab, Pohang, Gyeongbuk, South Korea
来源：
RECRYSTALLIZATION AND GRAIN GROWTH III, PTS 1 AND 2 | 2007年 / 558-559卷
关键词：
abnormal grain growth; Fe-3%Si steel; grain boundary; high angle annular dark field image; multi-phased precipitate;
D O I：
10.4028/www.scientific.net/MSF.558-559.1453
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The distribution of the precipitates on the grain boundaries in Fe-3%Si steel during secondary recrystallization annealing were studied using high-angle annular dark filed (HAADF) scanning transmission electron microscopy (STEM). Because HAADF image can show both grain boundaries and precipitates clearly, the change of precipitate distribution on grain boundaries can be quantitatively analyzed. It was observed that the total area of the precipitates on grain boundaries increased in the order of non-annealed, 600 degrees C, and 900 degrees C sample and the total area of precipitates on grain boundaries in the 1000 degrees C sample was much lower than that in the 900 degrees C sample. The compositions of the precipitates were also analyzed using X-ray energy-dispersive spectrometer (XEDS). The most precipitates were multi-phase ones, mainly composed of AIN and MnS. Our analysis results suggest that such a precipitate behavior is responsible for the abnormal grain growth of Fe-3%Si steel occurring under the temperature above 900 degrees C.
引用
收藏
页码：1453 / +
页数：2
相关论文
共 50 条
  • [21] Hydrogen Trapping by Dislocations and Grain Boundaries in Fe-3%Si AHoy
    Yuandong DIAO Shenyang Institute of Chemical Technology
    Journal of Materials Science & Technology, 1993, (05) : 385 - 387
  • [22] Misorientation characteristics of rapid moving boundaries during grain growth in Fe-3%Si alloys
    Mao, W.
    Yang, P.
    17TH INTERNATIONAL CONFERENCE ON TEXTURES OF MATERIALS (ICOTOM 17), 2015, 82
  • [23] Influence of Tensile Stress during Annealing on Primary Recrystallization Texture Development in Fe-3%Si Alloy
    Morishige, Nobusato
    Ushigami, Yoshiyuki
    Ushioda, Kohsaku
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2024, 110 (9-10): : 767 - 778
  • [24] Evolution of the texture on primary recrystallization and grain growth in Fe-3%Si steels
    Han, Kyu-Seok
    Park, Jong-Tae
    Kim, Jae-Kwan
    Szpunar, Jerzy A.
    RECRYSTALLIZATION AND GRAIN GROWTH III, PTS 1 AND 2, 2007, 558-559 : 747 - +
  • [25] EFFECT OF THE HEATING RATE DURING PRIMARY RECRYSTALLIZATION ON THE PROPERTIES OF THE ALLOY Fe-3% Si AFTER SECONDARY RECRYSTALLIZATION.
    Szymura, Stefan
    Zawada, Aleksandier
    1978, 23 (01): : 29 - 33
  • [26] The onset temperature of secondary recrystallization and the sharpness of Goss secondary recrystallization texture in the nitrided Fe-3%Si alloy
    Woo, JS
    Han, CH
    Hong, BD
    Harase, J
    ACTA MATERIALIA, 1998, 46 (14) : 4905 - 4909
  • [27] INFLUENCE OF SULFIDE STABILITY ON SECONDARY RECRYSTALLIZATION OF FE-3 PERCENT SI ALLOY
    IVANOVA, IM
    MOLOTILO.BV
    SAMARINA, NM
    STEEL IN THE USSR, 1974, 4 (01): : 76 - 78
  • [28] Influence of primary recrystallized structure on secondary recrystallization in Fe-3%Si alloy
    Ushigami, Y
    Yoshitomi, Y
    Takahashi, N
    GRAIN GROWTH IN POLYCRYSTALLINE MATERIALS II, PTS 1 AND 2, 1996, 204- : 623 - 628
  • [29] Effects of cold rolling reduction on secondary recrystallization of Fe-3%Si alloy
    Shimazu, T
    Arai, S
    Sakai, T
    Tsubakino, H
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2002, 88 (03): : 49 - 56
  • [30] Dynamic recrystallization by twinning mechanism in Fe-3%Si steel at high temperature
    Kaibyshev, R
    Kazakulov, I
    RECRYSTALLIZATION AND GRAIN GROWTH, VOLS 1 AND 2, 2001, : 943 - 948
12345