Effect of Temperature Variation on Wear Behaviour of Austenitic Stainless Steel

被引：2

作者：

Alias, S. K. ^{[1
]}

Ahmad, S. ^{[1
]}

Abdullah, B. ^{[1
]}

Pahroraji, H. F. ^{[1
]}

Hamami, G. ^{[1
]}

机构：

[1] Univ Teknol MARA Johor, Fac Mech Engn, Masai 81750, Johor, Malaysia

来源：

INTERNATIONAL ENGINEERING RESEARCH AND INNOVATION SYMPOSIUM (IRIS) | 2016年 / 160卷

关键词：

AISI; 4140; KINETICS;

D O I：

10.1088/1757-899X/160/1/012026

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The effects of boronizing temperatures on the wear and hardness properties of austenitic stainless steel were investigated in this study. The samples were prepared in accordance to standard samples preparation for wear and hardness test. Pack boronizing were conducted using EKabor (R) 1 powder medium at two different temperatures which are 850 degrees C and 950 degrees C. The wear resistance properties were evaluated though pin on disk test and the surface characterization was analyzed through scanning electron microscopy (SEM), observation. Vickers microhardness tester was performed to obtain the hardness of the samples. The results indicated that there are presences of FeB and Fe2B phases on both samples, but thicker FeB phase was produced at Po-950 samples. This resulted in reduction of abrasion wear properties but major improvement of the hardness properties of boronized stainless steel.

引用

页数：5

共 50 条

[31] Effect of ageing time on the creep behaviour of NiAl hardened austenitic stainless steel
Satyanarayana, DVV
Malakondaiah, G
Sarma, DS
[J]. TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2000, 53 (03): : 243 - 248
[32] Effect of annealing on corrosion behaviour of nitrogen S phase in austenitic stainless steel
Li, XY
Dong, H
[J]. MATERIALS SCIENCE AND TECHNOLOGY, 2003, 19 (10) : 1427 - 1434
[33] Effect of nitrogen doping on sliding wear behaviour of stainless steel coatings
Sun, Y
Kappaganthu, SR
[J]. TRIBOLOGY LETTERS, 2004, 17 (04) : 845 - 850
[34] Effect of intermetallic particles on wear behaviour of stainless steel matrix composites
Velasco, F
Lima, WM
Antón, N
Abenójar, J
Torralba, JM
[J]. TRIBOLOGY INTERNATIONAL, 2003, 36 (07) : 547 - 551
[35] TEMPERATURE EFFECT OF Xe ION IRRADIATION TO 316 AUSTENITIC STAINLESS STEEL
Huang Hefei
Li Jianjian
Liu Renduo
Chen Huaican
Yan Long
[J]. ACTA METALLURGICA SINICA, 2014, 50 (10) : 1189 - 1194
[36] High-Temperature Oxidation Behaviour of CrSi Coatings on 316 Austenitic Stainless Steel
Gurtaran, Mikdat
Zhang, Zhenxue
Li, Xiaoying
Dong, Hanshan
[J]. MATERIALS, 2023, 16 (09)
[37] Influence of temperature on multiaxial creep behaviour of 304HCu austenitic stainless steel
Sahoo, K. C.
Vijayanand, V. D.
Goyal, Sunil
Parameswaran, P.
Laha, K.
[J]. MATERIALS SCIENCE AND TECHNOLOGY, 2019, 35 (18) : 2181 - 2199
[38] High-temperature oxidation behaviour of nanostructure surface layered austenitic stainless steel
Singh, Digvijay
Cemin, Felipe
Jimenez, Mawin J. M.
Antunes, Vinicius
Alvarez, Fernando
Orlov, Dmytro
Figueroa, Carlos A.
Hosmani, Santosh S.
[J]. APPLIED SURFACE SCIENCE, 2022, 581
[39] The influence of temperature on the corrosion behaviour of high nitrogen austenitic stainless steel in chloride media
Tzaneva, B. R.
[J]. BULGARIAN CHEMICAL COMMUNICATIONS, 2014, 46 (02): : 378 - 383
[40] Behaviour of austenitic stainless steel bolts at elevated temperatures
Wang, Hui
Hu, Ying
Wang, Xing-Qiang
Tao, Zhong
Tang, Sheng-Lin
Pang, Xiao-Ping
Chen, Yohchia Frank
[J]. ENGINEERING STRUCTURES, 2021, 235

← 1 2 3 4 5 →