Densification and characterization of hot-pressed ZrC-based composite doped with Nb and CNT

被引：12

作者：

Li, Jian ^{[1
]}

Zhang, Zhaofu ^{[1
]}

Wang, Shouhao ^{[1
]}

Wang, Yongchang ^{[1
]}

Dai, Jixiang ^{[1
]}

Zu, Yufei ^{[1
]}

Sha, Jianjun ^{[1
]}

机构：

[1] Dalian Univ Technol, State Key Lab Struct Anal Ind Equipment, Dalian 116024, Peoples R China

来源：

MATERIALS & DESIGN | 2016年 / 104卷

基金：

高等学校博士学科点专项科研基金;

关键词：

ZrC; Nb; CNT; Microstructure; Mechanical properties; MECHANICAL-PROPERTIES; ENVIRONMENT; STRENGTH; BEHAVIOR; KINETICS; POWDERS;

D O I：

10.1016/j.matdes.2016.05.003

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

ZrC-based composite doped with 20 vol.% niobium (Nb) and 3 vol.% carbon nanotubes (CNT) was prepared by hot pressing. Due to the addition of Nb and CNT, the sinterability of ZrC was significantly improved, resulting in highly dense matrix (99.28%) at reduced sintering temperature (1600 degrees C). The flexural strength was 590 MPa at room temperature and 563 MPa at 800 degrees C, respectively. The fracture toughness was 7.23 MPa.m(1/2), which increased by 80% compared with the monolithic ZrC (4 MPa.m(1/2)). In addition, the work of fracture was calculated to be 267 J/m(2). Based on the microstructure characterizations, the improved fracture properties could be attributed to crack deflection, crack bridging and crack branching, which consumed more fracture energy during the fracture process. (C) 2016 Elsevier Ltd. All rights reserved.

引用

页码：43 / 50

页数：8

共 50 条

[41] Characterization of the Hot-Pressed Coal Briquettes Prepared with the HyperCoal
Wang, Yajie
Zuo, Haibin
Bai, Kaikai
Zhao, Jun
Chen, Jiansheng
ENERGY TECHNOLOGY 2020: RECYCLING, CARBON DIOXIDE MANAGEMENT, AND OTHER TECHNOLOGIES, 2020, : 57 - 67
[42] Characterization of Hot-pressed Poplar Wood with Chemical Pretreatment
Chen, Heyu
Lang, Qian
Feng, Zifeng
Xu, Yilin
Pu, Junwen
2012 INTERNATIONAL CONFERENCE ON BIOBASE MATERIAL SCIENCE AND ENGINEERING (BMSE), 2012, : 280 - 283
[43] STRUCTURAL CHARACTERIZATION OF HOT-PRESSED MANGANESE ALUMINUM SPINEL
SIDDIQI, SA
AKHTAR, P
MATEEN, A
MATERIALS LETTERS, 1987, 5 (11-12) : 475 - 478
[44] Hot-pressed, dry, composite, PEO-based electrolyte membranes I. Ionic conductivity characterization
Appetecchi, GB
Croce, F
Hassoun, J
Scrosati, B
Salomon, M
Cassel, F
JOURNAL OF POWER SOURCES, 2003, 114 (01) : 105 - 112
[45] The microstructure of an yttria-doped hot-pressed silicon nitride
Oliveira, FAC
Tambuyser, P
Baxter, DJ
CERAMICS INTERNATIONAL, 2000, 26 (06) : 571 - 578
[46] CHARACTERIZATION AND OXIDATION RESISTANCE OF HOT-PRESSED CHROMIUM DIBORIDE
EMILIANI, ML
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1993, 172 (1-2): : 111 - 124
[47] TEM AND HREM CHARACTERIZATION OF HOT-PRESSED ZIRCON CERAMICS
SHI, Y
HUANG, XX
RUAN, ML
YAN, DS
MATERIALS LETTERS, 1995, 23 (4-6) : 247 - 252
[48] Microstructure of an yttria-doped hot-pressed silicon nitride
Costa Oliveira, F.A., 2000, Elsevier Science Ltd, Exeter, United Kingdom (26)
[49] Influence of graphite nano-flakes on densification and mechanical properties of hot-pressed ZrB2-SiC composite
Asl, Mehdi Shahedi
Kakroudi, Mandi Ghassemi
Kondolaji, Rouhollah Abedi
Nasiri, Hadi
CERAMICS INTERNATIONAL, 2015, 41 (04) : 5843 - 5851
[50] MICROSTRUCTURE OF HOT-PRESSED ZINC-OXIDE DOPED WITH POTASSIUM
MORIYOSHI, Y
MARUYAMA, O
IKEGAMI, T
YAMAMURA, H
WATANABE, A
ZEITSCHRIFT FUR PHYSIKALISCHE CHEMIE-WIESBADEN, 1981, 125 (01): : 107 - 118

← 1 2 3 4 5 →