Preparation of High Entropy Alloy Cu29Zr32Ti15Al5Ni19 with High Glass Forming Ability

被引：2
|
作者：
Pi Jinhong [1 ]
He Xiancong [1 ]
Wang Zhangzhong [1 ]
机构：
[1] Nanjing Inst Technol, Jiangsu Key Lab Adv Struct Mat & Applicat Technol, Nanjing 211167, Jiangsu, Peoples R China
来源：
RARE METAL MATERIALS AND ENGINEERING | 2017年 / 46卷 / 07期
关键词：
high entropy alloy; bulk metallic glass; glass forming ability; compressive strength; BULK METALLIC-GLASS; THERMODYNAMIC ANALYSIS; MICROSTRUCTURE;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
High entropy alloy (HEA) Cu29Zr32Ti15Al5Ni19 consisting of two solid solution phases and bulk metallic glass (HE-BMG) with the same composition were prepared separately by casting in a copper mold. The results indicate that the alloy has high glass forming ability. The compressive strength of as cast HEA Cu29Zr32Ti15Al5Ni19 is 1127 MPa. HEA Cu29Zr32Ti15Al5Ni19 shows good tempering resistance. The hardness (HV) of Cu29Zr32Ti15Al5Ni19 remains 8260 MPa after it is treated at 750 degrees C for 2 h.
引用
收藏
页码：1810 / 1814
页数：5
相关论文
共 50 条
  • [31] Effect of be addition on glass forming ability and crystallization behaviors in amorphous Ti50Cu32Ni15Sn3 alloy
    Kim, YC
    Kim, WT
    Kim, DH
    PRICM 4: FORTH PACIFIC RIM INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS AND PROCESSING, VOLS I AND II, 2001, : 107 - 110
  • [32] Ultrastrong behaviors of a non-equiatomic Ti-Zr-Ni-Cu-Be high entropy metallic glass with ultrahigh glass forming ability (vol 577, 121323, 2022)
    Wang, Yuanyuan
    Zhu, Zhengwang
    Wang, Aimin
    Zhang, Haifeng
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2023, 604
  • [33] The relations between ΔTx and the glass forming ability of bulk amorphous Zr-Cu-Ni-Al-Hf-Ti and Zr52.5Cu17.9Ni 14.6Al10Ti5 alloys
    Xing, D. (xingdw@hope.hit.edu.cn), 1600, Elsevier Ltd (375): : 1 - 2
  • [34] Correlation between entropy and glass-forming ability of Cu-Zr and Cu-Zr-Al alloys
    Patel, K. Margi
    Malek, Irfan
    Shah, C. Mit
    Lad, N. Kirit
    Pratap, Arun
    MATERIALS TODAY-PROCEEDINGS, 2021, 47 : 587 - 591
  • [35] Thermodynamics of Zr52.5Cu17.9Ni14.6Al10Ti5 bulk metallic glass forming alloy
    Patel, Ashmi T.
    Shevde, Heena R.
    Pratap, Arun
    JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 2012, 107 (01) : 167 - 170
  • [36] Thermodynamics of Zr52.5Cu17.9Ni14.6Al10Ti5 bulk metallic glass forming alloy
    Ashmi T. Patel
    Heena R. Shevde
    Arun Pratap
    Journal of Thermal Analysis and Calorimetry, 2012, 107 : 167 - 170
  • [37] Co substituted Zr-Cu-Al-Ni metallic glasses with enhanced glass-forming ability and high plasticity
    Zhang, Yu
    Zhou, Min
    Zhao, Xiangyu
    Ma, Liqun
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2017, 473 : 120 - 124
  • [38] Ni-free Zr-Fe-Al-Cu bulk metallic glasses with high glass-forming ability
    Zhang, Q. S.
    Zhang, W.
    Inoue, A.
    SCRIPTA MATERIALIA, 2009, 61 (03) : 241 - 244
  • [39] Glass forming ability of Zr-based Zr-Cu-Ni-Al-(Ag) alloys
    Lyubenova, L.
    Rangelova, V.
    Spassova, M.
    Spassov, T.
    JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 2023, 148 (10) : 3975 - 3980
  • [40] Effects of addition of Al, Ti and Ag on glass-forming ability of Cu50Zr50 alloy
    Zhang, Qingsheng
    Zhang, Wei
    Inoue, Akihisa
    PRICM 6: SIXTH PACIFIC RIM INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS AND PROCESSING, PTS 1-3, 2007, 561-565 : 1333 - 1336
12345