We have developed a long Y-123 coated conductors by ion-beam-assisted deposition (IBAD) and pulsed-laser-deposition (PLD) method. Now, we can routinely obtained 100 m class Y-123 tapes with over 100 A at 77 K. For power applications using Y-123 conductors, coiling and cooling techniques are important elements. From 2004, we have developed and demonstrated a solenoid type coil that is the most suitable for practical application because it has advantage such as (1) uniformity of magnetic field (2) no joint. In this paper, we describe the development of conduction-cooled HTS test coil that has 14 turn x 22 layers using 100 m Y-123 conductors. In order to use the conduction cooling system, the Y-123 conductors were stabilized for 0.1 mm thick Cu tapes and spacers between the layers consisted of aluminum nitride in the coils. In the demonstration of this coil at 30 K, 40 K, 50 K, 60 K and 77 K by cryo-cooling system, the good cooling and superconducting performances were observed. The central magnetic fields of over 1 T were successfully obtained with operating currents of over 400 A and under 40 K. Furthermore, this coil was operated on additional magnetic fields of 3 T by combination of LTS magnets. The central magnetic fields of 0.5 T were generated from the cooled HTS coils with operating current of 190 A on additional magnetic fields of 3 T by LTS magnets at 30 K. Total magnetic fields were exceeded 3.5 T at 30 K. (C) 2007 Published by Elsevier B.V.