Influence of Deposition Time on ZnS Thin Films Performance with Chemical Bath Deposition

被引：13

作者：

Zhou, Limei ^{[1
]}

Tang, Nan ^{[1
]}

Wu, Sumei ^{[1
]}

Hu, Xiaofei ^{[1
]}

Xue, Yuzhi ^{[1
]}

机构：

[1] Dalian Jiaotong Univ, Sch Mat Sci & Engn, Dalian 116028, Peoples R China

来源：

2011 INTERNATIONAL CONFERENCE ON PHYSICS SCIENCE AND TECHNOLOGY (ICPST) | 2011年 / 22卷

关键词：

Chemical bath deposition; ZnS; Thin films; Deposition time; Annealed;

D O I：

10.1016/j.phpro.2011.11.055

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

ZnS thin films had been deposited by chemical bath deposition method onto glass substrates in alkaline liquor. The reaction solution is made of ZnSO4, NH4OH and SC(NH2)(2). Different deposition times (1 h, 1.5 h, 2 h, 2.5 h and 3 h) were selected to study the performance of ZnS thin films. As the results, the ZnS films' thickness were about 50-207 nm. XRD results showed an amorphous structure. Through comparing the surface morphology before and after annealing, it could be seen that annealing made some particles grow up and the surface smooth and even. The transmittance decreased with the increase of deposition time in the range of 300-800 nm. The transmittance of annealed ZnS film was lower than that of deposited one in the range of 300-800 nm. The ZnS band gap values were calculated in the range of 3.72-3.9 eV. (C) 2011 Published by Elsevier B.V. Selection and/or peer-review under responsibility of Garry Lee.

引用

页码：354 / 359

页数：6

共 50 条

[21] Crystalline ZnS thin films by chemical bath deposition method and its characterization
Roy, Poulomi
Ota, Jyoti R.
Srivastava, Suneel Kumar
[J]. THIN SOLID FILMS, 2006, 515 (04) : 1912 - 1917
[22] Oxygen free chemical bath deposition of ZnS thin films on (111) silicon
Tillotson, Brock
Richmond, Geraldine
Meitzner, Karl Jet
[J]. ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 2013, 245
[23] High quality antireflective ZnS thin films prepared by chemical bath deposition
Tec-Yam, S.
Rojas, J.
Rejon, V.
Oliva, A. I.
[J]. MATERIALS CHEMISTRY AND PHYSICS, 2012, 136 (2-3) : 386 - 393
[24] Nanocrystalline ZnS thin films by chemical bath deposition method and its characterization
Salim, S. M.
Eid, A. H.
Salem, A. M.
Abou El-Khair, H. M.
[J]. SURFACE AND INTERFACE ANALYSIS, 2012, 44 (08) : 1214 - 1218
[25] Effect of pH on the properties of ZnS thin films grown by chemical bath deposition
Ben Nasr, T
Kamoun, N
Kanzari, M
Bennaceur, R
[J]. THIN SOLID FILMS, 2006, 500 (1-2) : 4 - 8
[26] Effects of bath temperature on the properties of CdS and ZnS thin films deposited by Chemical bath deposition
Bai, Peng
Zhang, Gong
Zhuang, Daming
Ye, Yakuan
[J]. Taiyangneng Xuebao/Acta Energiae Solaris Sinica, 2014, 35 (03): : 481 - 486
[27] Influence of magnesium dopant on ZnS thin films by low-cost chemical bath deposition technique
Ashith, V. K.
Moger, Sahana Nagappa
[J]. OPTIK, 2023, 284
[28] Influence of Deposition Parameters on Cadmium Sulphide Thin Films Grown by Chemical Bath Deposition
Patel, Kinjal K.
Shah, Dimple
[J]. ADVANCED SCIENCE LETTERS, 2016, 22 (04) : 1071 - 1075
[29] EFFECT OF DEPOSITION TIME ON CHEMICAL BATH DEPOSITION PROCESS AND THICKNESS OF BaSe THIN FILMS
Okereke, N. A.
Ekpunobi, A. J.
[J]. JOURNAL OF OPTOELECTRONIC AND BIOMEDICAL MATERIALS, 2011, 3 (04): : 81 - 85
[30] The Optical and Electrical Characteristics of ZnS: In Thin Films Prepared by Chemical Bath Deposition Method
Long, Bo
Cheng, Shuying
Zhou, Haifang
Liao, Jie
Zhang, Hong
Jia, Hongjie
Li, Hongnan
[J]. ECS SOLID STATE LETTERS, 2014, 3 (11) : P140 - P143

← 1 2 3 4 5 →