Characterization of friction surfaced martensitic stainless steel (AISI 410) coatings

被引：22
|
作者：
Puli, Ramesh [1 ]
Kumar, E. Nandha [1 ]
Ram, G. D. Janaki [1 ]
机构：
[1] Indian Inst Technol, Mat Joining Lab, Dept Met & Mat Engn, Madras 600036, Tamil Nadu, India
来源：
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS | 2011年 / 64卷 / 1-2期
关键词：
friction surfacing; martensitic stainless steels; coatings; microstructure; TOOL STEEL; H13;
D O I：
10.1007/s12666-011-0008-6
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Friction surfacing is a candidate process for depositing corrosion and wear resistant coatings. Being a solid-state process, it offers several advantages over conventional fusion welding based surfacing process. In the current work, martensitic stainless steel AISI 410 was friction surfaced over mild steel substrates. Coating microstructures were characterized using light microscopy, scanning electron microscopy and Xray diffraction. Coatings in as-deposited condition exhibited a fully martensitic microstructure and were found to be quite hard (with an average hardness of 460 HV). Bend and shear tests indicated excellent coating/substrate bonding. Overall, the current work shows that martensitic stainless steel AISI 410 can be satisfactorily friction surfaced on mild steel.
引用
收藏
页码：41 / 45
页数：5
相关论文
共 50 条
  • [31] Phase transformation in AISI 410 stainless steel
    Tsai, MC
    Chiou, CS
    Du, JS
    Yang, JR
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2002, 332 (1-2): : 1 - 10
  • [32] Effect of Laser Beam Mode on the Microstructural Evolution in AISI 410 Martensitic Stainless Steel Welds
    Srinivasan, P. Bala
    LASERS IN ENGINEERING, 2008, 18 (5-6) : 351 - 359
  • [33] Effect of tempering temperature on impact energy of AISI 410 martensitic stainless steel at low temperatures
    Suwanpatcharakul, Kittipat
    Saenarjhan, Nithi
    Nakthong, Nathi
    Lothongkum, Anchaleeporn Waritswat
    Lothongkum, Gobboon
    MATERIALS TESTING, 2021, 63 (08) : 699 - 704
  • [34] EFFECT OF NITROGEN ON SOLIDIFICATION STRUCTURE OF CONTINUOUS CASTING AISI410 MARTENSITIC STAINLESS STEEL
    Zhou, Shu-cai
    Yang, Jie
    Yang, Yong-jun
    METALURGIA INTERNATIONAL, 2012, 17 (01): : 40 - 43
  • [35] Characterization of austenitic stainless steel friction surfaced deposit over low carbon steel
    Govardhan, D.
    Kumar, A. C. S.
    Murti, K. G. K.
    Reddy, G. Madhusudhan
    MATERIALS & DESIGN, 2012, 36 : 206 - 214
  • [36] 410 sintered martensitic stainless steel material
    Yang, Xiaoming
    Ji, Gongshe
    Ran, Xiaoguang
    Huang, Ke
    Zheng, Yueming
    Zhang, Zhenqi
    Fenmo Yejin Jishu/Powder Metallurgy Technology, 1988, 6 (03): : 173 - 179
  • [37] OPTIMIZATION OF CUTTING PARAMETERS OF MARTENSITIC STAINLESS STEEL GRADES AISI 410 AND AISI 420 DURING CNC DRY MILLING
    George, Pramod
    Selvaraj, D. Philip
    JOURNAL OF ENGINEERING SCIENCE AND TECHNOLOGY, 2021, 16 (06): : 4369 - 4382
  • [38] A comparative study of low temperature plasma nitriding, carburising and nitrocarburising of AISI 410 martensitic stainless steel
    Li, C. X.
    Bell, T.
    MATERIALS SCIENCE AND TECHNOLOGY, 2007, 23 (03) : 355 - 361
  • [39] Microstructure and corrosion behaviour of DC-pulsed plasma nitrided AISI 410 martensitic stainless steel
    Corengia, P
    Ybarra, G
    Moina, C
    Cabo, A
    Broitman, E
    SURFACE & COATINGS TECHNOLOGY, 2004, 187 (01): : 63 - 69
  • [40] Hot-Deformation Behavior and Hot-Processing Maps of AISI 410 Martensitic Stainless Steel
    Qi, Rong-Sheng
    Jin, Miao
    Guo, Bao-Feng
    Liu, Xin-Gang
    Chen, Lei
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2016, 35 (09) : 929 - 940
12345