Crack closure effects on fatigue crack growth thresholds and remaining life in an HSLA steel

被引：2
|
作者：
Todd, JA
Chen, L
Yankov, EY
Mostovoy, S
机构：
[1] TEXAS INSTRUMENTS INC, ATTLEBORO, MA USA
[2] A FINKL & SONS, CHICAGO, IL 60616 USA
来源：
JOURNAL OF PRESSURE VESSEL TECHNOLOGY-TRANSACTIONS OF THE ASME | 1997年 / 119卷 / 01期
关键词：
D O I：
10.1115/1.2842264
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The effects of crack closure on the near-threshold corrosion fatigue crack growth behavior of Mil S-24645 HSLA steel and its weld metal have been investigated in air, ASTM seawater at the free corrosion potential, and ASTM seawater at -0.8V and -1.0V (SCE) using frequencies of 10, 2, and 0.2 Hz, and a stress ratio, R = 0.1. Remaining life, in the presence and absence of crack closure, has been estimated as a function of applied stress range for a structure containing a 3-nm-deep surface semi-elliptical flaw.
引用
收藏
页码：37 / 44
页数：8
相关论文
共 50 条
  • [11] FATIGUE CRACK GROWTH AND CRACK CLOSURE IN VACUUM.
    Jono, Masahiro
    Song, Jiho
    Ohgaki, Masayoshi
    Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 1985, 51 (463): : 806 - 813
  • [12] THE INFLUENCE OF SLIP CHARACTER CRACK CLOSURE ON FATIGUE CRACK-GROWTH THRESHOLDS IN TITANIUM-ALLOYS
    ALLISON, JE
    WILLIAMS, JC
    JOURNAL OF METALS, 1983, 35 (08): : A36 - A36
  • [13] Fatigue Crack Growth Rate Behaviour of HSLA Steel at Varying Load Amplitudes
    Bandgar, Sachin
    Gupta, Chiradeep
    Rao, Gaurav
    Malik, Pranshu
    Singh, R. N.
    Sridhar, K.
    2ND INTERNATIONAL CONFERENCE ON STRUCTURAL INTEGRITY AND EXHIBITION 2018 (SICE 2018), 2019, 14 : 330 - 336
  • [14] Microstructural effects on crack closure and propagation thresholds of small fatigue cracks
    Akiniwa, Y
    Tanaka, K
    Kimura, H
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2001, 24 (12) : 817 - 829
  • [15] On generating fatigue crack growth thresholds
    Forth, SC
    Newman, JC
    Forman, RG
    INTERNATIONAL JOURNAL OF FATIGUE, 2003, 25 (01) : 9 - 15
  • [16] Acoustic emission studies for characterization of fatigue crack growth behavior in HSLA steel
    Kumar, Jalaj
    Ahmad, S.
    Mukhopadhyay, C. K.
    Jayakumar, T.
    Kumar, Vikas
    NONDESTRUCTIVE TESTING AND EVALUATION, 2016, 31 (01) : 77 - 96
  • [17] Effect of band-overload on fatigue crack growth rate of HSLA steel
    Abhinay, S. V.
    Tenduwe, Om Prakash
    Kumar, Ajit
    Dutta, K.
    Verma, B. B.
    Ray, P. K.
    4TH NATIONAL CONFERENCE ON PROCESSING AND CHARACTERIZATION OF MATERIALS, 2015, 75
  • [18] Evaluation of overload effects on fatigue crack growth and closure
    Borrego, LP
    Ferreira, JM
    da Cruz, JMP
    Costa, JM
    ENGINEERING FRACTURE MECHANICS, 2003, 70 (11) : 1379 - 1397
  • [19] Estimating Remaining Fatigue Life of Critical Members of Steel Railway Bridges using Fatigue Crack Growth Model
    Viththagan, V.
    Wimalasiri, R. J.
    Karunananda, P. A. K.
    ENGINEER-JOURNAL OF THE INSTITUTION OF ENGINEERS SRI LANKA, 2023, 56 (03): : 33 - 41
  • [20] Environmental effects on fatigue crack development in HSLA steel and fine grain α-titanium
    Marsh, P.G., 1600, Pergamon Press Inc, Tarrytown, NY, United States (33):
12345