Electrochemical Analysis of AA6082 Aluminium Alloy in Chloride Media

被引：12
|
作者：
Xhanari, Klodian [1 ,2 ]
Finsgar, Matjaz [1 ]
机构：
[1] Univ Maribor, Fac Chem & Chem Engn, Smetanova Ulica 17, SLO-2000 Maribor, Slovenia
[2] Univ Tirana, Fac Nat Sci, Blvd Zogu 1, Tirana 1001, Albania
来源：
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE | 2017年 / 12卷 / 07期
关键词：
corrosion; interfaces; aluminium alloy; weight loss; electrochemical impedance spectroscopy; cyclic polarisation; CORROSION BEHAVIOR; AL-ALLOY; PRECIPITATION; STEEL; ACID;
D O I：
10.20964/2017.07.71
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
AA6082 aluminium alloy is widely used in the automotive industry. The aim of this study was to report on the corrosion behaviour of this alloy in 1 and 5 wt.% NaCl solutions at 50 degrees C and to compare it to the results in the same solution at room temperature, using the weight loss and electrochemical techniques. The chosen concentration and temperature range are the most severe conditions in automotive corrosion tests. The localised and general corrosion rates are higher for the highest of the two temperatures tested. At both temperatures, corrosion occurs according to a kinetic-controlled process.
引用
收藏
页码：5845 / 5853
页数：9
相关论文
共 50 条
  • [21] A study of microstructure and mechanical properties of friction stir welding aluminium alloy AA6082 with Zn interlayer
    Singh, Avtar
    Kumar, Vinod
    Grover, Neel Kanth
    MATERIALS RESEARCH EXPRESS, 2019, 6 (11)
  • [22] Adhesive joining of aluminium AA6082: The effects of resin and surface treatment
    Borsellino, C.
    Di Bella, G.
    Ruisi, V. F.
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2009, 29 (01) : 36 - 44
  • [23] Effects of lubricant on the IHTC during the hot stamping of AA6082 aluminium alloy: Experimental and modelling studies
    Liu, Xiaochuan
    El Fakir, Omer
    Meng, Lichun
    Sun, Xiaoguang
    Li, Xiaodong
    Wang, LiLiang
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2018, 255 : 175 - 183
  • [24] Mechanical properties of the AlSi1MgMn aluminium alloy (AA6082) processed by gradation rolling
    Neugebauer, R.
    Sterzing, A.
    Bergmann, M.
    MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 2011, 42 (07) : 593 - 598
  • [25] Intermetallic phase selection during homogenization for AA6082 alloy
    Li, J. H.
    Wimmer, A.
    Dehm, G.
    Schumacher, P.
    PHILOSOPHICAL MAGAZINE, 2014, 94 (08) : 830 - 846
  • [26] Flow modelling of AA 6082 aluminium alloy
    Bruni, C
    Forcellese, A
    Gabrielli, F
    AMST 02: ADVANCED MANUFACTURING SYSTEMS AND TECHNOLOGY, PROCEEDINGS, 2002, (437): : 367 - 374
  • [27] Adhesive joining of aluminium AA6082: The effects of resin and surface treatment
    Borsellino, C.
    Di Bella, G.
    Ruisi, V.F.
    International Journal of Adhesion and Adhesives, 2009, 29 (01): : 36 - 44
  • [28] Grain structure control of flat extruded AA6082 alloy
    Furu, Trond
    Vatne, Hans Erik
    Materials Science Forum, 2000, 331
  • [29] Grain structure control of flat extruded AA6082 alloy
    Furu, T
    Vatne, HE
    ALUMINIUM ALLOYS: THEIR PHYSICAL AND MECHANICAL PROPERTIES, PTS 1-3, 2000, 331-3 : 843 - 848
  • [30] Joining of non-weldable AA7075 and weldable AA6082 aluminium alloy sheets by Friction Stir Welding
    Kovacs, Zsolt
    Hareancz, Ferenc
    XXIII INTERNATIONAL CONFERENCE ON MANUFACTURING (MANUFACTURING 2018), 2018, 448
12345