Electrochemical Analysis of AA6082 Aluminium Alloy in Chloride Media

被引：12
|
作者：
Xhanari, Klodian [1 ,2 ]
Finsgar, Matjaz [1 ]
机构：
[1] Univ Maribor, Fac Chem & Chem Engn, Smetanova Ulica 17, SLO-2000 Maribor, Slovenia
[2] Univ Tirana, Fac Nat Sci, Blvd Zogu 1, Tirana 1001, Albania
来源：
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE | 2017年 / 12卷 / 07期
关键词：
corrosion; interfaces; aluminium alloy; weight loss; electrochemical impedance spectroscopy; cyclic polarisation; CORROSION BEHAVIOR; AL-ALLOY; PRECIPITATION; STEEL; ACID;
D O I：
10.20964/2017.07.71
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
AA6082 aluminium alloy is widely used in the automotive industry. The aim of this study was to report on the corrosion behaviour of this alloy in 1 and 5 wt.% NaCl solutions at 50 degrees C and to compare it to the results in the same solution at room temperature, using the weight loss and electrochemical techniques. The chosen concentration and temperature range are the most severe conditions in automotive corrosion tests. The localised and general corrosion rates are higher for the highest of the two temperatures tested. At both temperatures, corrosion occurs according to a kinetic-controlled process.
引用
收藏
页码：5845 / 5853
页数：9
相关论文
共 50 条
  • [1] The Corrosion Inhibition of AA6082 Aluminium Alloy by Certain Azoles in Chloride Solution: Electrochemistry and Surface Analysis
    Xhanari, Klodian
    Finsgar, Matjaz
    COATINGS, 2019, 9 (06):
  • [2] Mechanical behaviour of an AA6082 aluminium alloy at low temperatures
    Westermann, Ida
    Hopperstad, Odd Sture
    Langseth, Magnus
    ALUMINIUM ALLOYS 2014 - ICAA14, 2014, 794-796 : 532 - +
  • [3] Integrated Casting-Extrusion (ICE) of an AA6082 Aluminium Alloy
    Khorsand, Shohreh
    Huang, Yan
    LIGHT METALS 2017, 2017, : 235 - 241
  • [4] Characterization of deformation behaviour of aluminium alloy AA6082 processed by HPT
    Zrnik, J.
    Kraus, L.
    Scheriau, S.
    Pippan, R.
    Ciesar, M.
    KOVOVE MATERIALY-METALLIC MATERIALS, 2012, 50 (05): : 319 - 325
  • [5] Fracture initiation and propagation in fatigue contact loading of AA6082 aluminium alloy
    Benedetti, Angela
    Molari, Pier Gabriele
    Morelli, Piero
    FRACTURE AND DAMAGE MECHANICS V, PTS 1 AND 2, 2006, 324-325 : 1091 - +
  • [6] Effect of Ultrasonic Processing on a Direct Chill Cast AA6082 Aluminium Alloy
    Salloum-Abou-Jaoude, G.
    Eskin, D. G.
    Barbatti, C.
    Jarry, P.
    Jarrett, M.
    Fan, Z.
    LIGHT METALS 2017, 2017, : 997 - 1003
  • [7] Experimental investigation on aluminium alloy AA6082 and AA2014 using the friction stir welding
    Praneetha, Kyama
    Apoorva, Maddela
    Laxmi, Thumpuru Prasanna
    Sekhar, S. Ravi
    Sashank, S. Sravan
    MATERIALS TODAY-PROCEEDINGS, 2022, 62 : 3397 - 3404
  • [8] STRUCTUAL EVOLUTION IN ALUMINIUM ALLOY AA6082 DURING HPT DEFORMATION AT INCREASED TEMPERATURE
    Zrnik, Jozef
    Kraus, Libor
    Scheriau, Stephan
    Pippan, Reinhard
    PROCEEDINGS OF THE 13TH INTERNATIONAL CONFERENCE ON ALUMINUM ALLOYS (ICAA13), 2012, : 1613 - 1620
  • [9] Microstructure and mechanical properties of the AA6082 aluminium alloy with small additions of Sc and Zr
    Vlach, Martin
    Smola, Bohumil
    Stulikova, Ivana
    Ocenasek, Vladivoj
    INTERNATIONAL JOURNAL OF MATERIALS RESEARCH, 2009, 100 (03) : 420 - 423
  • [10] Superhydrophobic behaviour of modified AA6082 alloy surfaces
    Calabrese, L.
    Khaskhoussi, A.
    Proverbio, E.
    METALLURGIA ITALIANA, 2019, 111 (11-12): : 6 - 10
12345