Preparation and properties of DLC/MoS2 multilayer coatings for high humidity tribology

被引：24
|
作者：
Zhao, Xiaoyu [1 ,3 ]
Lu, Zhibin [1 ]
Wu, Guizhi [1 ]
Zhang, Guangan [1 ]
Wang, Liping [1 ,2 ]
Xue, Qunji [1 ]
机构：
[1] Chinese Acad Sci, Lanzhou Inst Chem Phys, State Key Lab Solid Lubricat, Lanzhou 730000, Peoples R China
[2] Chinese Acad Sci, Ningbo Inst Mat Technol & Engn, Key Lab Marine Mat & Related Technol, Key Lab Marine Mat & Protect Technol Zhejiang Pro, Ningbo 315201, Zhejiang, Peoples R China
[3] Chinese Acad Sci, Grad Univ, Beijing 100049, Peoples R China
来源：
MATERIALS RESEARCH EXPRESS | 2016年 / 3卷 / 06期
基金：
中国国家自然科学基金;
关键词：
DLC; MoS2; humidity; multilayer; tribology; COMPOSITE COATINGS; MECHANICAL-PROPERTIES; MOS2; FILMS; CARBON-FILMS; MICROSTRUCTURE; WEAR; ORIENTATION; PERFORMANCE; OXIDATION; FRICTION;
D O I：
10.1088/2053-1591/3/6/066401
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The DLC/MoS2 multilayer coatings with different modulus ratios were deposited by magnetron sputtering in this study. The morphology, structure, composition, mechanical properties and tribological properties were investigated using several analytical techniques (FESEM, AFM, TEM, AES, XPS, nanoindentation and high humidity tribological test). The results showed that the well-defined multilayer coatings were composed of densely packed particles in which many nanocrystallines with some kinds of defects were distributed in matrix. The incorporation of oxygen into the lattice led to the degraded chemical stability. The coating's hardness and elastic modulus were almost in the same range. Moderate improvement on the high humidity tribological properties were obtained, which was important for the extension of the service life of MoS2 in humid air.
引用
收藏
页数：11
相关论文
共 50 条
  • [31] On the possibility of improving antifriction properties of MoS2 coatings by alloying
    Semenov, A. P.
    JOURNAL OF FRICTION AND WEAR, 2012, 33 (02) : 160 - 165
  • [32] On the possibility of improving antifriction properties of MoS2 coatings by alloying
    A. P. Semenov
    Journal of Friction and Wear, 2012, 33 : 160 - 165
  • [33] Preparation, modification and nonlinear optical properties of semiconducting MoS2 and MoS2/ZnO composite film
    Liu, Hai-Quan
    Yao, Cheng-Bao
    Jiang, Cai-Hong
    Wang, Xue
    OPTICS AND LASER TECHNOLOGY, 2021, 138
  • [34] Preparation and tribological properties of MoS2/graphite composite coatings modified by La2O3
    Qiu, Ming
    Zhang, Rui
    Li, Yingchun
    Du, Hui
    Pang, Xiao Xu
    INDUSTRIAL LUBRICATION AND TRIBOLOGY, 2018, 70 (08) : 1422 - 1430
  • [35] Effect of relative humidity and temperature on the tribology of multilayer micro/nanocrystalline CVD diamond coatings
    Shabani, M.
    Abreu, C. S.
    Gomes, J. R.
    Silva, R. F.
    Oliveira, F. J.
    DIAMOND AND RELATED MATERIALS, 2017, 73 : 190 - 198
  • [36] Preparation and tribological properties of Ni/DLC multilayer film
    Wu, Yanxia
    Qi, Jiawei
    Li, Ke
    Zhou, Xiaoyan
    Yu, Shengwang
    Zhang, Caili
    Liu, Ying
    JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A, 2024, 42 (02):
  • [37] Structure, Mechanical and Tribological Properties of MoSN/MoS2 Multilayer Films
    Fu, Yanlong
    He, Tengfei
    Yang, Wu
    Xu, Jiao
    Mu, Bo
    Pang, Xianjuan
    Wang, Peng
    COATINGS, 2019, 9 (02):
  • [38] Microstructure and tribological properties of WS2/MoS2 multilayer films
    Zhu Li-na
    Wang Cheng-biao
    Wang Hai-dou
    Xu Bin-shi
    Zhuang Da-ming
    Liu Jia-jun
    Li Guo-lu
    APPLIED SURFACE SCIENCE, 2012, 258 (06) : 1944 - 1948
  • [39] WC/DLC/WS2 nanocomposite coatings for aerospace tribology
    A.A. Voevodin
    J.P. O'Neill
    J.S. Zabinski
    Tribology Letters, 1999, 6 : 75 - 78
  • [40] Tribological properties of Cr- and Ti-doped MoS2 composite coatings under different humidity atmosphere
    Ding, Xing-zhao
    Zeng, X. T.
    He, X. Y.
    Chen, Z.
    SURFACE & COATINGS TECHNOLOGY, 2010, 205 (01): : 224 - 231
12345