Effect of manganese content and microstructure on the susceptibility of X70 pipeline steel to hydrogen cracking

被引：113

作者：

Hejazi, D. ^{[1
]}

Haq, A. J. ^{[1
]}

Yazdipour, N. ^{[1
]}

Dunne, D. P. ^{[1
]}

Calka, A. ^{[1
]}

Barbaro, F. ^{[2
]}

Pereloma, E. V. ^{[1
]}

机构：

[1] Univ Wollongong, Sch Mech Mat & Mechatron Engn, Wollongong, NSW 2522, Australia

[2] BlueScope Steel Ltd, Port Kembla, NSW 2505, Australia

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2012年 / 551卷

基金：

澳大利亚研究理事会;

关键词：

Pipeline steel; Microstructure; Hydrogen charging; Fracture toughness; Fractography; Inclusions; THERMOMECHANICAL CONTROL PROCESS; STRESS-CORROSION CRACKING; TIC PARTICLES; FRACTURE; DIFFUSION; INCLUSIONS; RESISTANCE; EMBRITTLEMENT; CHARACTER; TOUGHNESS;

D O I：

10.1016/j.msea.2012.04.076

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The influence of composition and microstructure on susceptibility to hydrogen induced cracking (HIC) was investigated in high strength pipeline steels, with Mn contents of 1.2% (standard, X70), and 0.5% (medium, MX70). The HIC resistance of the simulated coarse grained heat affected zone microstructures and normalized X70 transfer bar was also investigated. Notched and fatigue pre-cracked samples were charged with hydrogen prior to three point bend tests. The conditional fracture toughness J(Q) was determined. The results are discussed in relation to grain size, microstructure, composition and the type and distribution of non-metallic inclusions and precipitates. (C) 2012 Elsevier BM. All rights reserved.

引用

页码：40 / 49

页数：10

共 50 条

[21] Effect of hydrostatic pressure on hydrogen behavior on the surface of X70 pipeline steel
Xu, Zhengyi
Zhang, Pengyuan
Zhang, Bo
Lei, Bing
Feng, Zhiyuan
Wang, Junyi
Shao, Yawei
Meng, Guozhe
Wang, Yanqiu
Wang, Fuhui
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 25 : 5907 - 5916
[22] Effect of hydrogen charging on Charpy impact toughness of an X70 pipeline steel
Cauwels, Margo
Depraetere, Robin
De Waele, Wim
Hertele, Stijn
Verbeken, Kim
Depover, Tom
23 EUROPEAN CONFERENCE ON FRACTURE, ECF23, 2022, 42 : 977 - 984
[23] Effects of hydrogen on the fracture toughness of a X70 pipeline steel
Wang, Rong
CORROSION SCIENCE, 2009, 51 (12) : 2803 - 2810
[24] Modeling bulk diffusion of hydrogen in X70 pipeline steel
Andreas Drexler
Sergio Pastore
Josef Domitner
Scientific Reports, 15 (1)
[25] Effect of hydrogen-induced plasticity on the stress corrosion cracking of X70 pipeline steel in simulated soil environments
Liu, Z. Y.
Wang, X. Z.
Du, C. W.
Li, J. K.
Li, X. G.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 658 : 348 - 354
[26] Bauschinger effect of X70 pipeline steel plates
Li, Dian-Jie
Han, Bao-Yun
Guo, Feng
Kang T'ieh/Iron and Steel (Peking), 2005, 40 (10): : 76 - 79
[27] Effect of microstructure and inclusions on hydrogen induced cracking susceptibility and hydrogen trapping efficiency of X120 pipeline steel
Huang, F.
Liu, J.
Deng, Z. J.
Cheng, J. H.
Lu, Z. H.
Li, X. G.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (26): : 6997 - 7001
[28] Hydrogen induced cracking behaviors of X70 pipeline steel and its welds under electrochemical charging
Zhang Yingrui
Dong Chaofang
Li Xiaogang
Rui Xiaolong
Zhou Herong
ACTA METALLURGICA SINICA, 2006, 42 (05) : 521 - 527
[29] Evaluation of hydrogen induced cracking behavior of API X70 pipeline steel at different heat treatments
Mohtadi-Bonab, M. A.
Szpunar, J. A.
Collins, L.
Stankievech, R.
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2014, 39 (11) : 6076 - 6088
[30] Hydrogen induced cracking behaviors of X70 pipeline steel and its welds under electrochemical charging
College of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China
不详
Jinshu Xuebao, 2006, 5 (521-527):

← 1 2 3 4 5 →